Summary for Test 2023-07-19-22-2
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 215666 DEA: 11430564 EFIS: 1119000015 |
---|---|
DIST-CO-RTE-PM | 11-SD-67-R6.0/24.4 |
Award Date | 03/01/2022 |
Closeout Date | 11/04/2024 |
Work Description | COLD PLANE, RHMA OVERLAY AND HFST, AND INSTALL CHANNELIZERS. |
Location Description | SAN DIEGO COUNTY NEAR LAKESIDE AND RAMONA FROM 0.2 MILE NORTH OF SAN DIEGO RIVER BRIDGE TO ROUTE 78 |
QA Service Level | 1 (Verified on 07/06/2021) |
Sample Information
Sample Taken Date | 07/19/2023 | Sample Unique Key | 22 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 07/20/2023 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
Title of sampler | Quality Control Manager | Telephone number of sampler | 17076245467 |
Laboratory sample identification | 943816 | Linked DIME Sample ID | 943816 |
The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | 1472974 |
---|---|---|---|
Batch Number | 1472974 | Mix Number | 1472974 |
Resin Binder Type | Polyester | Used for Overlay | Yes |
Used for Inlay | No |
Test Details
DIME Sample ID: 2023-07-19-22
DIME Test ID: 2023-07-19-22-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2023-10-17
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 07/26/2023
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.484 in
Sample 1 Thickness: 0.148 in
Sample 1 Area: 0.0716 in^2
Sample 1 Ultimate Strength Actual: 275.8 lbs
Sample 1 percent elongation: 57.645 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.489 in
Sample 2 Thickness: 0.138 in
Sample 2 Area: 0.0675 in^2
Sample 2 Ultimate Strength Actual: 243.9 lbs
Sample 2 percent elongation: 49.518 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.489 in
Sample 3 Thickness: 0.154 in
Sample 3 Area: 0.0753 in^2
Sample 3 Ultimate Strength Actual: 293.4 lbs
Sample 3 percent elongation: 53.112 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.484 in
Sample 4 Thickness: 0.146 in
Sample 4 Area: 0.0707 in^2
Sample 4 Ultimate Strength Actual: 263.6 lbs
Sample 4 percent elongation: 49.923 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.489 in
Sample 5 Thickness: 0.137 in
Sample 5 Area: 0.067 in^2
Sample 5 Ultimate Strength Actual: 264.6 lbs
Sample 5 percent elongation: 57.106 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.489 in
Sample 6 Thickness: 0.145 in
Sample 6 Area: 0.0709 in^2
Sample 6 Ultimate Strength Actual: 239.7 lbs
Sample 6 percent elongation: 43.311 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3852 psi
Sample 2 Ultimate strength : 3613.3 psi
Sample 3 Ultimate strength: 3896.4 psi
Sample 4 Ultimate strength: 3728.4 psi
Sample 5 Ultimate strength: 3949.3 psi
Sample 6 Ultimate strength : 3380.8 psi
Ultimate Strength Average: 3737 psi
Percent Elongation Average: 52 %
General comments (publicly viewable) (Max 1000 characters): Accepted vendor's results.
Test was verified on 10/17/2023 ✔