Summary for Test 2024-07-15-59-3
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 995535 DEA: 120T8704 EFIS: 1222000110 |
|---|---|
| DIST-CO-RTE-PM | 12-ORA-5,57-30.3/39.6,10.7/21.8 |
| Award Date | 03/01/2024 |
| Closeout Date | 06/23/2025 |
| Work Description | APPLY METHACRYLATE, POLYESTER CONCRETE, AND REPLACE JOINT SEALS. |
| Location Description | ORANGE COUNTY AT VARIOUS LOCATIONS ON ROUTE 5 FROM ROUTE 5/55 SEPARATION TO EUCLID STREET OVERCROSSING AND ON ROUTE 57 FROM ROUTE 5/57 SEPARATION TO TONNER CANYON ROAD UNDERCROSSING |
| QA Service Level | 1 (Verified on 01/26/2024) |
Sample Information
| Sample Taken Date | 07/15/2024 | Sample Unique Key | 59 |
|---|---|---|---|
| Date that the sample was received by the laboratory/organization performing the testing | 07/16/2024 | Sample type | Quality Control |
| A brief description of the sample | 1 gallon can / PPC 1121 RESIN | The quantity of what the sample constitutes | 2 tankers |
| From where was the sample collected | Source | First name of sampler or witnessed by | Gilberto |
| Last name of sampler or witnessed by | Gonzalez | Title of sampler | Quality Control Manager |
| Telephone number of sampler | 7076245467 | Laboratory sample identification | 000092KBP |
| Linked DIME Sample ID | 000092KBP | The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia |
| Transportation Laboratory (TL) Number | Sacramento Caltrans lab | Inspector Lot Number from the Transportation Laboratory (TL) Form | |
| Structure unique identifier | Structure name | ||
| Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | AZ4G01015 |
|---|---|---|---|
| Batch Number | AZ4G01015 | Mix number | AZ4G01015 |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2024-07-15-59
DIME Test ID: 2024-07-15-59-3
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2024-08-08
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 07/18/2024
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.487 in
Sample 1 Thickness: 0.244 in
Sample 1 Area: 0.1188 in^2
Sample 1 Ultimate Strength Actual: 419.483 lbs
Sample 1 percent elongation: 41.1 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.486 in
Sample 2 Thickness: 0.26 in
Sample 2 Area: 0.1264 in^2
Sample 2 Ultimate Strength Actual: 434.563 lbs
Sample 2 percent elongation: 50.2 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.487 in
Sample 3 Thickness: 0.259 in
Sample 3 Area: 0.1261 in^2
Sample 3 Ultimate Strength Actual: 430.127 lbs
Sample 3 percent elongation: 58.7 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.497 in
Sample 4 Thickness: 0.257 in
Sample 4 Area: 0.1277 in^2
Sample 4 Ultimate Strength Actual: 428.306 lbs
Sample 4 percent elongation: 50.9 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.507 in
Sample 5 Thickness: 0.259 in
Sample 5 Area: 0.1313 in^2
Sample 5 Ultimate Strength Actual: 426.331 lbs
Sample 5 percent elongation: 58.3 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.509 in
Sample 6 Thickness: 0.253 in
Sample 6 Area: 0.1288 in^2
Sample 6 Ultimate Strength Actual: 420.274 lbs
Sample 6 percent elongation: 65 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3531 psi
Sample 2 Ultimate strength : 3438 psi
Sample 3 Ultimate strength: 3411 psi
Sample 4 Ultimate strength: 3354 psi
Sample 5 Ultimate strength: 3247 psi
Sample 6 Ultimate strength : 3263 psi
Ultimate Strength Average: 3374 psi
Percent Elongation Average: 54 %
General comments (publicly viewable) (Max 1000 characters): Accepted vendor's results
Test was verified on 8/8/2024 ✔