Summary for Test 2024-07-19-34-3
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 995445 DEA: 043W5204 EFIS: 0421000384 |
|---|---|
| DIST-CO-RTE-PM | 04-ALA-580,680,880-VAR |
| Award Date | 01/24/2024 |
| Closeout Date | 02/02/2026 |
| Work Description | PLACE POLYESTER CONCRETE OVERLAY AND REPLACE JOINT SEAL. |
| Location Description | ALAMEDA COUNTY AT VARIOUS LOCATIONS |
| QA Service Level | 1 (Verified on 11/16/2023) |
Sample Information
| Sample Taken Date | 07/19/2024 | Sample Unique Key | 34 |
|---|---|---|---|
| Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 07/23/2024 |
| Sample type | Quality Control | A brief description of the sample | 1 gallon can / PPC 1121 RESIN |
| The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
| First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
| Title of sampler | Quality Control Manager | Telephone number of sampler | 7076245467 |
| Laboratory sample identification | 000098KBP | Linked DIME Sample ID | 000098KBP |
| The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
| Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
| Structure name | Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | AZ4G01065 |
|---|---|---|---|
| Batch Number | AZ4G01065 | Mix number | AZ4G01065 |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2024-07-19-34
DIME Test ID: 2024-07-19-34-3
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2024-08-07
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 07/25/2024
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.485 in
Sample 1 Thickness: 0.271 in
Sample 1 Area: 0.1314 in^2
Sample 1 Ultimate Strength Actual: 370.022 lbs
Sample 1 percent elongation: 63.6 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.485 in
Sample 2 Thickness: 0.275 in
Sample 2 Area: 0.1334 in^2
Sample 2 Ultimate Strength Actual: 386.86 lbs
Sample 2 percent elongation: 67.3 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.487 in
Sample 3 Thickness: 0.247 in
Sample 3 Area: 0.1203 in^2
Sample 3 Ultimate Strength Actual: 372.81 lbs
Sample 3 percent elongation: 71.2 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.486 in
Sample 4 Thickness: 0.264 in
Sample 4 Area: 0.1283 in^2
Sample 4 Ultimate Strength Actual: 407.481 lbs
Sample 4 percent elongation: 75.1 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.486 in
Sample 5 Thickness: 0.265 in
Sample 5 Area: 0.1288 in^2
Sample 5 Ultimate Strength Actual: 403.273 lbs
Sample 5 percent elongation: 73.8 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.486 in
Sample 6 Thickness: 0.267 in
Sample 6 Area: 0.1298 in^2
Sample 6 Ultimate Strength Actual: 365.776 lbs
Sample 6 percent elongation: 63.7 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 2816 psi
Sample 2 Ultimate strength : 2900 psi
Sample 3 Ultimate strength: 3099 psi
Sample 4 Ultimate strength: 3176 psi
Sample 5 Ultimate strength: 3131 psi
Sample 6 Ultimate strength : 2818 psi
Ultimate Strength Average: 2990 psi
Percent Elongation Average: 69 %
General comments (publicly viewable) (Max 1000 characters): Accepted Vendor's Results
Test was verified on 8/7/2024 ✔