Summary for Test 2024-06-26-103-3
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 995445 DEA: 043W5204 EFIS: 0421000384 |
|---|---|
| DIST-CO-RTE-PM | 04-ALA-580,680,880-VAR |
| Award Date | 01/24/2024 |
| Closeout Date | Not set |
| Work Description | PLACE POLYESTER CONCRETE OVERLAY AND REPLACE JOINT SEAL. |
| Location Description | ALAMEDA COUNTY AT VARIOUS LOCATIONS |
| QA Service Level | 1 (Verified on 11/16/2023) |
Sample Information
| Sample Taken Date | 06/26/2024 | Sample Unique Key | 103 |
|---|---|---|---|
| Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 06/28/2024 |
| Sample type | Quality Control | A brief description of the sample | 1 gallon can / PPC 1121 RESIN |
| The quantity of what the sample constitutes | 34 Totes | From where was the sample collected | Source |
| First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
| Title of sampler | Quality Control Manager | Telephone number of sampler | 7076245467 |
| Laboratory sample identification | 000087KBP | Linked DIME Sample ID | 000087KBP |
| The fabricator/manufacturer/facility name | Kwik Bond Polymers | Transportation Laboratory (TL) Number | |
| Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
| Structure name | Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | AZ4F00956T |
|---|---|---|---|
| Batch number | AZ4F00956T | Mix number | AZ4F00956T |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2024-06-26-103
DIME Test ID: 2024-06-26-103-3
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2024-08-01
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 07/01/2024
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.486 in
Sample 1 Thickness: 0.249 in
Sample 1 Area: 0.121 in^2
Sample 1 Ultimate Strength Actual: 382.844 lbs
Sample 1 percent elongation: 69.9 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.486 in
Sample 2 Thickness: 0.249 in
Sample 2 Area: 0.121 in^2
Sample 2 Ultimate Strength Actual: 342.43 lbs
Sample 2 percent elongation: 51.9 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.486 in
Sample 3 Thickness: 0.256 in
Sample 3 Area: 0.1244 in^2
Sample 3 Ultimate Strength Actual: 382.406 lbs
Sample 3 percent elongation: 68.4 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.486 in
Sample 4 Thickness: 0.254 in
Sample 4 Area: 0.1234 in^2
Sample 4 Ultimate Strength Actual: 407.59 lbs
Sample 4 percent elongation: 74.8 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.486 in
Sample 5 Thickness: 0.259 in
Sample 5 Area: 0.1259 in^2
Sample 5 Ultimate Strength Actual: 388.905 lbs
Sample 5 percent elongation: 69.4 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.486 in
Sample 6 Thickness: 0.255 in
Sample 6 Area: 0.1239 in^2
Sample 6 Ultimate Strength Actual: 367.24 lbs
Sample 6 percent elongation: 64.8 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3164 psi
Sample 2 Ultimate strength : 2830 psi
Sample 3 Ultimate strength: 3074 psi
Sample 4 Ultimate strength: 3303 psi
Sample 5 Ultimate strength: 3089 psi
Sample 6 Ultimate strength : 2964 psi
Ultimate Strength Average: 3071 psi
Percent Elongation Average: 67 %
General comments (publicly viewable) (Max 1000 characters): Accepted vendor's results
Test was verified on 8/1/2024 ✔