Summary for Test 2022-09-02-35-2
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 215682 DEA: 031H1904 EFIS: 0316000065 |
---|---|
DIST-CO-RTE-PM | 03-SAC-80,244-M9.6/12.9,0.0/T0.8 |
Award Date | 06/18/2021 |
Closeout Date | Not set |
Work Description | COLD PLANE AC PAVEMENT, PLACE RHMA AND INDIVIDUAL SLAB REPLACEMENT. |
Location Description | SACRAMENTO COUNTY IN AND NEAR SACRAMENTO ON ROUTE 80 FROM 0.2 MILE EAST OF LONGVIEW DRIVE OVERCROSSING TO 0.4 MILE EAST OF MADISON AVENUE OVERCROSSING AND ON ROUTE 244 FROM 0.3 MILE NORTH OF AUBURN BOULEVARD TO CONNECTOR TO ROUTE 80 |
QA Service Level | 1 (Verified on 05/17/2021) |
Sample Information
Sample Taken Date | 09/02/2022 | Sample Unique Key | 35 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 09/06/2022 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 32 Totes | From where was the sample collected | Source |
First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
Title of sampler | Quality Control Manager | Telephone number of sampler | 17076245467 |
Laboratory sample identification | 943123 | Linked DIME Sample ID | 943123 |
The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | 1426034 |
---|---|---|---|
Batch Number | 1426034 | Mix Number | 1426034 |
Resin Binder Type | Polyester | Used for Overlay | Yes |
Used for Inlay | No |
Test Details
DIME Sample ID: 2022-09-02-35
DIME Test ID: 2022-09-02-35-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2023-03-29
Test Results
Number of specimens tested: 5
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 09/15/2022
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.483 in
Sample 1 Thickness: 0.16 in
Sample 1 Area: 0.0773 in^2
Sample 1 Ultimate Strength Actual: 322.8 lbs
Sample 1 percent elongation: 66.12 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.483 in
Sample 2 Thickness: 0.146 in
Sample 2 Area: 0.0705 in^2
Sample 2 Ultimate Strength Actual: 269.3 lbs
Sample 2 percent elongation: 56.23 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.491 in
Sample 3 Thickness: 0.134 in
Sample 3 Area: 0.0658 in^2
Sample 3 Ultimate Strength Actual: 256.6 lbs
Sample 3 percent elongation: 58.84 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.491 in
Sample 4 Thickness: 0.151 in
Sample 4 Area: 0.0741 in^2
Sample 4 Ultimate Strength Actual: 294.4 lbs
Sample 4 percent elongation: 62.06 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.484 in
Sample 5 Thickness: 0.151 in
Sample 5 Area: 0.0731 in^2
Sample 5 Ultimate Strength Actual: 300.8 lbs
Sample 5 percent elongation: 65.22 %
Sample 5 Time: 0 MM:SS
Sample 1 Ultimate strength: 4175.9 psi
Sample 2 Ultimate strength : 3819.9 psi
Sample 3 Ultimate strength: 3899.7 psi
Sample 4 Ultimate strength: 3973 psi
Sample 5 Ultimate strength: 4114.9 psi
Ultimate Strength Average: 3997 psi
Percent Elongation Average: 62 %
General comments (publicly viewable) (Max 1000 characters): Accepted vendor's results.
Test was verified on 3/29/2023 ✔