DIME » All Projects » Project - DEA: AML-CEM » Sample 2023-04-18-25 » Sample Details

Sample Record

DIME Sample ID 2023-04-18-25

Project Information

Project IdentifiersProject ID: 8801
DEA: AML-CEM
EFIS: AML-CEM
DIST-CO-RTE-PM59---
Award DateNot set
Closeout DateNot set
Work DescriptionSpecial project for Cementitious Materials for use in Concrete Authorized Material List (AML)
Location DescriptionNot set
QA Service LevelNOT VERIFIED

Owner Lab

  • CT HQ - Sacramento Cement Testing Laboratory

Sample Information

Sample Taken Date04/18/2023 Sample Unique Key25
Date that the sample was received by the laboratory/organization performing the testing04/18/2023 Sample typeAnnual Source Testing
A brief description of the sampleClass N Pozzolan The quantity of what the sample constitutes1 Bucket
From where was the sample collectedSource First name of sampler or witnessed byN/A
Last name of sampler or witnessed byNA Title of sampler
Telephone number of sampler Laboratory sample identificationCM235305
Linked DIME Sample ID The fabricator/manufacturer/facility nameGolden State Pozzolan
Transportation Laboratory (TL) Number Inspector Lot Number from the Transportation Laboratory (TL) Form
Structure unique identifier Structure name
Bid ItemNot set

Material Information

Material TypeCementitious BrandGolden State Pozzolan
MillGSP Class N Pozzolan Type of Cementitious MaterialClass F or N Flyash

Submitted Tests

DIME Test IDTest MethodTester Name, Testing LabDate TestedDate AddedVerified?Release DateTest CommentsPrivacy LevelActions
2023-04-18-25-1ASTM C109-21: Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)AV, CT HQ - Sacramento Cement Testing Laboratory05/16/202306/20/2023
No
7 day
2023-04-18-25-2ASTM C109-21: Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)AV, CT HQ - Sacramento Cement Testing Laboratory06/06/202306/06/2023
No
Specimen 3 was eliminated from the average for being outside allowable limits per ASTM C109
2023-04-18-25-3ASTM C1567-13: Standard Test Method for Determining the Potential Alkali-Silica Reactivity of Combinations of Cementitious Materials and Aggregate (Accelerated Mortar-Bar Method)Benjamin Lenz, CT HQ - Sacramento Cement Testing Laboratory05/30/202306/20/2023
No
Specimen 3 was broken at demolding. Specimen 3 readings above are fictional to make the average length change correct.
2023-04-18-25-4ASTM C430-8: Standard Test Method for Fineness of Hydraulic Cement by the 45-μm (No. 325) SieveAnthony Valdez, CT HQ - Sacramento Cement Testing Laboratory04/27/202306/20/2023
No
2023-04-18-25-5ASTM C1567-13: Standard Test Method for Determining the Potential Alkali-Silica Reactivity of Combinations of Cementitious Materials and Aggregate (Accelerated Mortar-Bar Method)Benjamin Lenz, CT HQ - Sacramento Cement Testing Laboratory07/19/202308/04/2023
No
Borosilicate Glass Aggregate Glass agg has density of 2.23 so mass of glass agg reduced to 833g per sect. 8.5.3 of ASTM C1567.
2023-04-18-25-6ASTM C1567-13: Standard Test Method for Determining the Potential Alkali-Silica Reactivity of Combinations of Cementitious Materials and Aggregate (Accelerated Mortar-Bar Method)Benjamin Lenz, CT HQ - Sacramento Cement Testing Laboratory07/19/202308/04/2023
No
Five Bridges Natural Aggregate (Known Reactive)

Sample File Attachments

File NameExtensionDate UploadedActions
No results found.

Test File Attachments


DIME Test ID: 2023-04-18-25-1 ASTM C109-21
DIME Test ID: 2023-04-18-25-2 ASTM C109-21
DIME Test ID: 2023-04-18-25-3 ASTM C1567-13
DIME Test ID: 2023-04-18-25-4 ASTM C430-8
DIME Test ID: 2023-04-18-25-5 ASTM C1567-13
DIME Test ID: 2023-04-18-25-6 ASTM C1567-13