Summary for Test 2019-07-01-3-4
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 213858 DEA: 120Q9204 EFIS: 1217000127 |
---|---|
DIST-CO-RTE-PM | 12-ORA-57,91-var |
Award Date | 02/20/2019 |
Closeout Date | 02/19/2020 |
Work Description | METHACRYLATE DECK SEAL TREATMENT & POLYESTER CONC. OVERLAY |
Location Description | ORANGE COUNTY AT VARIOUS LOCATIONS |
QA Service Level | 1 (Verified on 05/03/2019) |
Sample Information
Sample Taken Date | 07/01/2019 | Sample Unique Key | 3 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 07/01/2019 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 36 Totes | From where was the sample collected | Source |
First name of sampler or witnessed by | Chris | Last name of sampler or witnessed by | Nunes |
Title of sampler | Telephone number of sampler | ||
Laboratory sample identification | Linked DIME Sample ID | ||
The fabricator/manufacturer/facility name | Kwik Bond Polymers and Reichhold | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Polyester | Mfg. Lot Number(s) | 1192076 |
---|---|---|---|
Batch number | 1192076 | Mix number | 1192076 |
Test Details
DIME Sample ID: 2019-07-01-3
DIME Test ID: 2019-07-01-3-4
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2019-07-08
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Ruben Macias
Date of test: 07/08/2019
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.486 in
Sample 1 Thickness: 0.238 in
Sample 1 Area: 0.1157 in^2
Sample 1 Ultimate Strength Actual: 443 lbs
Sample 1 percent elongation: 70 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.486 in
Sample 2 Thickness: 0.249 in
Sample 2 Area: 0.121 in^2
Sample 2 Ultimate Strength Actual: 426 lbs
Sample 2 percent elongation: 64.42 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.486 in
Sample 3 Thickness: 0.241 in
Sample 3 Area: 0.1171 in^2
Sample 3 Ultimate Strength Actual: 412 lbs
Sample 3 percent elongation: 63.04 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.485 in
Sample 4 Thickness: 0.244 in
Sample 4 Area: 0.1183 in^2
Sample 4 Ultimate Strength Actual: 406 lbs
Sample 4 percent elongation: 57.76 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.486 in
Sample 5 Thickness: 0.242 in
Sample 5 Area: 0.1176 in^2
Sample 5 Ultimate Strength Actual: 418 lbs
Sample 5 percent elongation: 64.59 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.486 in
Sample 6 Thickness: 0.243 in
Sample 6 Area: 0.1181 in^2
Sample 6 Ultimate Strength Actual: 418 lbs
Sample 6 percent elongation: 63.9 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3828.9 psi
Sample 2 Ultimate strength : 3520.7 psi
Sample 3 Ultimate strength: 3518.4 psi
Sample 4 Ultimate strength: 3432 psi
Sample 5 Ultimate strength: 3554.4 psi
Sample 6 Ultimate strength : 3539.4 psi
Ultimate Strength Average: 3566 psi
Percent Elongation Average: 64 %
General comments (publicly viewable) (Max 1000 characters):
Test was verified on 7/8/2019 ✔