Summary for Test 2022-11-17-61-2
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 215150 DEA: 120P0304 EFIS: 1215000024 |
---|---|
DIST-CO-RTE-PM | 12-ORA-74-11.5/16.6 |
Award Date | 11/13/2020 |
Closeout Date | Not set |
Work Description | PLACE HIGH FRICTION SURFACE TREATMENT, HMA & MIDWEST GUARDRAIL SYSTEM. |
Location Description | ORANGE COUNTY NEAR SAN JUAN CAPISTRANO FROM 1.0 MILE WEST OF SAN JUAN HOT SPRINGS ROAD TO ORANGE COUNTY LINE |
QA Service Level | 1 (Verified on 12/10/2020) |
Sample Information
Sample Taken Date | 11/17/2022 | Sample Unique Key | 61 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 12/15/2022 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
Title of sampler | Quality Control Manager | Telephone number of sampler | 17076245467 |
Laboratory sample identification | 943761 | Linked DIME Sample ID | 943761 |
The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | 1440299 |
---|---|---|---|
Batch Number | 1440299 | Mix Number | 1440299 |
Resin Binder Type | Polyester | Used for Overlay | Yes |
Used for Inlay | No |
Test Details
DIME Sample ID: 2022-11-17-61
DIME Test ID: 2022-11-17-61-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2023-06-29
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 11/28/2022
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.13 in
Sample 1 Thickness: 0.493 in
Sample 1 Area: 0.0641 in^2
Sample 1 Ultimate Strength Actual: 274.2 lbs
Sample 1 percent elongation: 66.707 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.133 in
Sample 2 Thickness: 0.492 in
Sample 2 Area: 0.0654 in^2
Sample 2 Ultimate Strength Actual: 237.8 lbs
Sample 2 percent elongation: 47.459 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.14 in
Sample 3 Thickness: 0.492 in
Sample 3 Area: 0.0689 in^2
Sample 3 Ultimate Strength Actual: 277.9 lbs
Sample 3 percent elongation: 59.065 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.139 in
Sample 4 Thickness: 0.491 in
Sample 4 Area: 0.0682 in^2
Sample 4 Ultimate Strength Actual: 288.2 lbs
Sample 4 percent elongation: 62.924 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.147 in
Sample 5 Thickness: 0.488 in
Sample 5 Area: 0.0717 in^2
Sample 5 Ultimate Strength Actual: 297.5 lbs
Sample 5 percent elongation: 61.306 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.134 in
Sample 6 Thickness: 0.49 in
Sample 6 Area: 0.0657 in^2
Sample 6 Ultimate Strength Actual: 276.8 lbs
Sample 6 percent elongation: 61.18 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 4277.7 psi
Sample 2 Ultimate strength : 3636.1 psi
Sample 3 Ultimate strength: 4033.4 psi
Sample 4 Ultimate strength: 4225.8 psi
Sample 5 Ultimate strength: 4149.2 psi
Sample 6 Ultimate strength : 4213.1 psi
Ultimate Strength Average: 4089 psi
Percent Elongation Average: 60 %
General comments (publicly viewable) (Max 1000 characters): Accepted supplier's results.
Test was verified on 6/29/2023 ✔