Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 994289 DEA: 042Q2504 EFIS: 0418000442 |
---|---|
DIST-CO-RTE-PM | 04-ALA-80,580,680-Various |
Award Date | 12/13/2022 |
Closeout Date | Not set |
Work Description | HIGH FRICTION SURFACE TREATMENT. |
Location Description | ALAMEDA COUNTY ON ROUTE 80,580 AND 680 AT VARIOUS LOCATIONS |
QA Service Level | 1 (Verified on 10/14/2022) |
Sample Information
Sample Taken Date | 05/30/2023 | Sample Unique Key | 25 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 05/31/2023 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 32 Totes | From where was the sample collected | Source |
First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
Title of sampler | Quality Control Manager | Telephone number of sampler | 17076245467 |
Laboratory sample identification | 943802 | Linked DIME Sample ID | 943802 |
The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | 1472348 |
---|---|---|---|
Batch Number | 1472348 | Mix Number | 1472348 |
Resin Binder Type | Polyester | Used for Overlay | Yes |
Used for Inlay | No |
Test Details
DIME Sample ID: 2023-05-30-25
DIME Test ID: 2023-05-30-25-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2023-06-28
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 06/06/2023
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.145 in
Sample 1 Thickness: 0.485 in
Sample 1 Area: 0.0703 in^2
Sample 1 Ultimate Strength Actual: 261.7 lbs
Sample 1 percent elongation: 61.1 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.149 in
Sample 2 Thickness: 0.487 in
Sample 2 Area: 0.0726 in^2
Sample 2 Ultimate Strength Actual: 282.3 lbs
Sample 2 percent elongation: 66.7 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.148 in
Sample 3 Thickness: 0.486 in
Sample 3 Area: 0.0719 in^2
Sample 3 Ultimate Strength Actual: 277.7 lbs
Sample 3 percent elongation: 65.9 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.145 in
Sample 4 Thickness: 0.487 in
Sample 4 Area: 0.0706 in^2
Sample 4 Ultimate Strength Actual: 255.9 lbs
Sample 4 percent elongation: 61.4 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.142 in
Sample 5 Thickness: 0.493 in
Sample 5 Area: 0.07 in^2
Sample 5 Ultimate Strength Actual: 229 lbs
Sample 5 percent elongation: 48.4 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.152 in
Sample 6 Thickness: 0.485 in
Sample 6 Area: 0.0737 in^2
Sample 6 Ultimate Strength Actual: 252.5 lbs
Sample 6 percent elongation: 55.9 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3722.6 psi
Sample 2 Ultimate strength : 3888.4 psi
Sample 3 Ultimate strength: 3862.3 psi
Sample 4 Ultimate strength: 3624.6 psi
Sample 5 Ultimate strength: 3271.4 psi
Sample 6 Ultimate strength : 3426.1 psi
Ultimate Strength Average: 3633 psi
Percent Elongation Average: 60 %
General comments (publicly viewable) (Max 1000 characters): Accepted supplier's results.
Test was verified on 6/28/2023 ✔