Summary for Test 2022-12-01-12-2
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 215150 DEA: 120P0304 EFIS: 1215000024 |
---|---|
DIST-CO-RTE-PM | 12-ORA-74-11.5/16.6 |
Award Date | 11/13/2020 |
Closeout Date | Not set |
Work Description | PLACE HIGH FRICTION SURFACE TREATMENT, HMA & MIDWEST GUARDRAIL SYSTEM. |
Location Description | ORANGE COUNTY NEAR SAN JUAN CAPISTRANO FROM 1.0 MILE WEST OF SAN JUAN HOT SPRINGS ROAD TO ORANGE COUNTY LINE |
QA Service Level | 1 (Verified on 12/10/2020) |
Sample Information
Sample Taken Date | 12/01/2022 | Sample Unique Key | 12 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 12/02/2022 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
Title of sampler | Quality Control Manager | Telephone number of sampler | 17076245467 |
Laboratory sample identification | 943762 | Linked DIME Sample ID | 943762 |
The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | 1442534 |
---|---|---|---|
Batch Number | 1442534 | Mix Number | 1442534 |
Resin Binder Type | Polyester | Used for Overlay | Yes |
Used for Inlay | No |
Test Details
DIME Sample ID: 2022-12-01-12
DIME Test ID: 2022-12-01-12-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2023-06-28
Test Results
Number of specimens tested: 5
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 11/08/2022
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.494 in
Sample 1 Thickness: 0.137 in
Sample 1 Area: 0.0677 in^2
Sample 1 Ultimate Strength Actual: 259 lbs
Sample 1 percent elongation: 59 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.484 in
Sample 2 Thickness: 0.142 in
Sample 2 Area: 0.0687 in^2
Sample 2 Ultimate Strength Actual: 293.3 lbs
Sample 2 percent elongation: 70.57 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.484 in
Sample 3 Thickness: 0.141 in
Sample 3 Area: 0.0682 in^2
Sample 3 Ultimate Strength Actual: 274.8 lbs
Sample 3 percent elongation: 64.24 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.483 in
Sample 4 Thickness: 0.137 in
Sample 4 Area: 0.0662 in^2
Sample 4 Ultimate Strength Actual: 275.9 lbs
Sample 4 percent elongation: 68.28 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.484 in
Sample 5 Thickness: 0.146 in
Sample 5 Area: 0.0707 in^2
Sample 5 Ultimate Strength Actual: 285.2 lbs
Sample 5 percent elongation: 64.74 %
Sample 5 Time: 0 MM:SS
Sample 1 Ultimate strength: 3825.7 psi
Sample 2 Ultimate strength : 4269.3 psi
Sample 3 Ultimate strength: 4029.3 psi
Sample 4 Ultimate strength: 4167.7 psi
Sample 5 Ultimate strength: 4033.9 psi
Ultimate Strength Average: 4065 psi
Percent Elongation Average: 65 %
General comments (publicly viewable) (Max 1000 characters): Accepted supplier's results.
Test was verified on 6/28/2023 ✔