Summary for Test 2022-04-22-28-3
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 993509 DEA: 101K9604 EFIS: 1019000163 |
---|---|
DIST-CO-RTE-PM | 10-MER,SJ,TUO-99,205,120-Var |
Award Date | 02/24/2022 |
Closeout Date | 10/06/2022 |
Work Description | REPLACE HMA PAVEMENT AND APPLY HIGH FRICTION SURFACE TREATMENT. |
Location Description | MERCED, SAN JOAQUIN, AND TUOLUMNE COUNTIES AT VARIOUS LOCATIONS |
QA Service Level | 1 (Verified on 01/18/2022) |
Sample Information
Sample Taken Date | 04/22/2022 | Sample Unique Key | 28 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 04/22/2022 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 32 Totes | From where was the sample collected | Source |
First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
Title of sampler | QC Technician | Telephone number of sampler | 7076245467 |
Laboratory sample identification | 943109 | Linked DIME Sample ID | |
The fabricator/manufacturer/facility name | Kwik Bond Polymers and Polynt | Transportation Laboratory (TL) Number | 943109 |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | T01401975 |
---|---|---|---|
Batch Number | T01401975 | Mix Number | T01401975 |
Resin Binder Type | Polyester | Used for Overlay | No |
Used for Inlay | No |
Test Details
DIME Sample ID: 2022-04-22-28
DIME Test ID: 2022-04-22-28-3
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2022-06-30
Test Results
Number of specimens tested: 5
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 05/05/2022
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.146 in
Sample 1 Thickness: 0.483 in
Sample 1 Area: 0.0705 in^2
Sample 1 Ultimate Strength Actual: 265.6 lbs
Sample 1 percent elongation: 67 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.154 in
Sample 2 Thickness: 0.495 in
Sample 2 Area: 0.0762 in^2
Sample 2 Ultimate Strength Actual: 260.5 lbs
Sample 2 percent elongation: 61.8 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.147 in
Sample 3 Thickness: 0.485 in
Sample 3 Area: 0.0713 in^2
Sample 3 Ultimate Strength Actual: 247.1 lbs
Sample 3 percent elongation: 62.6 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.146 in
Sample 4 Thickness: 0.484 in
Sample 4 Area: 0.0707 in^2
Sample 4 Ultimate Strength Actual: 251.6 lbs
Sample 4 percent elongation: 64.1 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.143 in
Sample 5 Thickness: 0.484 in
Sample 5 Area: 0.0692 in^2
Sample 5 Ultimate Strength Actual: 182.8 lbs
Sample 5 percent elongation: 54.7 %
Sample 5 Time: 0 MM:SS
Sample 1 Ultimate strength: 3767.4 psi
Sample 2 Ultimate strength : 3418.6 psi
Sample 3 Ultimate strength: 3465.6 psi
Sample 4 Ultimate strength: 3558.7 psi
Sample 5 Ultimate strength: 2641.6 psi
Ultimate Strength Average: 3370 psi
Percent Elongation Average: 62 %
General comments (publicly viewable) (Max 1000 characters): Accepted vendor's results.
Gel Time (ASTM C881) = 19 minutes
Cure Rate (ASTM D1640) = 1.35 hours
Test was verified on 6/30/2022 ✔