Summary for Test 2021-11-24-4-4

Test performed: ASTM D638-Dec14

Project Information

Project IdentifiersProject ID: 213406
DEA: 030F2504
EFIS: 0300000075
DIST-CO-RTE-PM03-YOL,SAC-80-R11.1/R11.7,M0.0/M0.5
Award Date08/21/2020
Closeout DateNot set
Work DescriptionSAC RIVER BOH (BRYTE BEND)
Location DescriptionSACRAMENTO AND YOLO COUNTIES IN WEST SACRAMENTO AND SACRAMENTO FROM 0.1 MILE WEST OF REED AVENUE UNDERCROSSING TO 0.1 MILE EAST OF SACRAMENTO RIVER BRIDGE AND OVERHEAD
QA Service Level1 (Verified on 06/07/2018)

Sample Information

Sample Taken Date11/24/2021 Sample Unique Key4
Will the laboratory/organization for which you are a member perform testing on this material sample?Yes Date that the sample was received by the laboratory/organization performing the testing11/24/2021
Sample typeQuality Control A brief description of the sample1 gallon can
The quantity of what the sample constitutes2 tankers From where was the sample collectedSource
First name of sampler or witnessed byDaniel Last name of sampler or witnessed byTikusis
Title of samplerTechnical Director Telephone number of sampler17073309227
Laboratory sample identification Linked DIME Sample ID
The fabricator/manufacturer/facility nameKwik Bond Polymers and Polynt Transportation Laboratory (TL) NumberSacramento Caltrans lab
Inspector Lot Number from the Transportation Laboratory (TL) Form Structure unique identifier
Structure name

Material Information

Material TypePolyester Mfg. Lot Number(s)1374041
Batch number1374041 Mix number1374041

Test Details

DIME Sample ID: 2021-11-24-4
DIME Test ID: 2021-11-24-4-4
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2021-12-10

Test Results


Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 12/01/2021
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.488 in
Sample 1 Thickness: 0.252 in
Sample 1 Area: 0.123 in^2
Sample 1 Ultimate Strength Actual: 469 lbs
Sample 1 percent elongation: 68.09 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.487 in
Sample 2 Thickness: 0.252 in
Sample 2 Area: 0.1227 in^2
Sample 2 Ultimate Strength Actual: 448 lbs
Sample 2 percent elongation: 63.8 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.485 in
Sample 3 Thickness: 0.24 in
Sample 3 Area: 0.1164 in^2
Sample 3 Ultimate Strength Actual: 417 lbs
Sample 3 percent elongation: 51.65 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.487 in
Sample 4 Thickness: 0.246 in
Sample 4 Area: 0.1198 in^2
Sample 4 Ultimate Strength Actual: 452 lbs
Sample 4 percent elongation: 66.87 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.485 in
Sample 5 Thickness: 0.26 in
Sample 5 Area: 0.1261 in^2
Sample 5 Ultimate Strength Actual: 465 lbs
Sample 5 percent elongation: 64.95 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.486 in
Sample 6 Thickness: 0.256 in
Sample 6 Area: 0.1244 in^2
Sample 6 Ultimate Strength Actual: 458 lbs
Sample 6 percent elongation: 65.74 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3813 psi
Sample 2 Ultimate strength : 3651.2 psi
Sample 3 Ultimate strength: 3582.5 psi
Sample 4 Ultimate strength: 3773 psi
Sample 5 Ultimate strength: 3687.5 psi
Sample 6 Ultimate strength : 3681.7 psi
Ultimate Strength Average:3698 psi
Percent Elongation Average:64 %
General comments (publicly viewable) (Max 1000 characters): Accepted vendor's results.

Test was verified on 12/10/2021