Test 2020-07-24-4-4 (ASTM D638-Dec14) Summary

Project Information
Project IdentifiersProject ID: 214687
DEA: 031G4904
EFIS: 0318000241
DIST-CO-RTE-PM03-ED,PLA,SAC,YOL-49,50,80-Var
Work DescriptionREPLACE JOINT SEALS AND PLACE POLYESTER CONCRETE OVERLAY.
Location DescriptionEL DORADO, PLACER, SACRAMENTO, AND YOLO COUNTIES AT VARIOUS LOCATIONS
Sample Information
Sample Taken Date7/24/2020 Sample Unique Key4
Will the laboratory/organization for which you are a member perform testing on this material sample?Yes Date that the sample was received by the laboratory/organization performing the testing7/24/2020
Sample typeQuality Control A brief description of the sample1 gallon can
The quantity of what the sample constitutes2 Tankers From where was the sample collectedSource
First name of sampler or witnessed byDaniel Last name of sampler or witnessed byTikusis
Title of samplerTechnical Director Laboratory sample identification
The fabricator/manufacturer/facility nameKwik Bond Polymers and Reichhold Transportation Laboratory (TL) NumberSacramento Caltrans lab
Inspector Lot Number from the Transportation Laboratory (TL) Form Structure unique identifier
Structure name
Material Information
Material TypePolyester Mfg. Lot Number(s)1267219
Batch number1267219 Mix number1267219
Test Details
DIME Sample ID: 2020-07-24-4
DIME Test ID: 2020-07-24-4-4
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2020-10-19
Test Results

Number of specimens tested: 6
Input Type: Measured
Tester's full name: Larry McCrum
Date of test: 10/19/2020
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.483 in
Sample 1 Thickness: 0.266 in
Sample 1 Area: 0.1285 in^2
Sample 1 Ultimate Strength Actual: 406.1 lbs
Sample 1 percent elongation: 60.48 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.483 in
Sample 2 Thickness: 0.261 in
Sample 2 Area: 0.1261 in^2
Sample 2 Ultimate Strength Actual: 398 lbs
Sample 2 percent elongation: 61.63 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.484 in
Sample 3 Thickness: 0.264 in
Sample 3 Area: 0.1278 in^2
Sample 3 Ultimate Strength Actual: 430.8 lbs
Sample 3 percent elongation: 65.54 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.482 in
Sample 4 Thickness: 0.264 in
Sample 4 Area: 0.1272 in^2
Sample 4 Ultimate Strength Actual: 415.9 lbs
Sample 4 percent elongation: 63.32 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.482 in
Sample 5 Thickness: 0.258 in
Sample 5 Area: 0.1244 in^2
Sample 5 Ultimate Strength Actual: 411 lbs
Sample 5 percent elongation: 64.35 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.483 in
Sample 6 Thickness: 0.253 in
Sample 6 Area: 0.1222 in^2
Sample 6 Ultimate Strength Actual: 393.5 lbs
Sample 6 percent elongation: 62.02 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3160.3 psi
Sample 2 Ultimate strength : 3156.2 psi
Sample 3 Ultimate strength: 3370.9 psi
Sample 4 Ultimate strength: 3269.7 psi
Sample 5 Ultimate strength: 3303.9 psi
Sample 6 Ultimate strength : 3220.1 psi
Ultimate Strength Average:3247 psi
Percent Elongation Average:63 %
General comments (publicly viewable) (Max 1000 characters):

Test was verified on 10/19/2020