Summary for Test 2019-06-12-2-7
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 213937 DEA: 023H8004 EFIS: 0218000037 |
---|---|
DIST-CO-RTE-PM | 02-SIS-5,96-VAR |
Award Date | 04/08/2019 |
Closeout Date | 12/04/2019 |
Work Description | REPLACE POLYESTER CONCRETE OVERLAY, APPLY METHACRYLATE, MGS. |
Location Description | SISKIYOU COUNTY AT VARIOUS LOCATIONS |
QA Service Level | 1 (Verified on 04/03/2019) |
Sample Information
Sample Taken Date | 06/12/2019 | Sample Unique Key | 2 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 06/12/2019 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | Chris | Last name of sampler or witnessed by | Nunes |
Title of sampler | Telephone number of sampler | ||
Laboratory sample identification | Linked DIME Sample ID | ||
The fabricator/manufacturer/facility name | Kwik bond and Reichhold | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Polyester | Mfg. Lot Number(s) | 1189324 |
---|---|---|---|
Batch number | 1189324 | Mix number | 1189324 |
Test Details
DIME Sample ID: 2019-06-12-2
DIME Test ID: 2019-06-12-2-7
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2019-07-01
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Larry McCrum
Date of test: 07/01/2019
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.485 in
Sample 1 Thickness: 0.246 in
Sample 1 Area: 0.1193 in^2
Sample 1 Ultimate Strength Actual: 444.8 lbs
Sample 1 percent elongation: 70.9 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.485 in
Sample 2 Thickness: 0.245 in
Sample 2 Area: 0.1188 in^2
Sample 2 Ultimate Strength Actual: 451 lbs
Sample 2 percent elongation: 73.9 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.484 in
Sample 3 Thickness: 0.249 in
Sample 3 Area: 0.1205 in^2
Sample 3 Ultimate Strength Actual: 401 lbs
Sample 3 percent elongation: 65.3 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.485 in
Sample 4 Thickness: 0.256 in
Sample 4 Area: 0.1242 in^2
Sample 4 Ultimate Strength Actual: 430 lbs
Sample 4 percent elongation: 65.2 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0 in
Sample 5 Thickness: 0 in
Sample 5 Area: 0 in^2
Sample 5 Ultimate Strength Actual: 0 lbs
Sample 5 percent elongation: 0 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.484 in
Sample 6 Thickness: 0.248 in
Sample 6 Area: 0.12 in^2
Sample 6 Ultimate Strength Actual: 394 lbs
Sample 6 percent elongation: 61.2 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3728.4 psi
Sample 2 Ultimate strength : 3796.3 psi
Sample 3 Ultimate strength: 3327.8 psi
Sample 4 Ultimate strength: 3462.2 psi
Sample 5 Ultimate strength: 0 psi
Sample 6 Ultimate strength : 3283.3 psi
Ultimate Strength Average: 2933 psi
Percent Elongation Average: 56 %
General comments (publicly viewable) (Max 1000 characters):
Test was verified on 7/1/2019 ✔