Test 2021-03-25-9-3 (ASTM D638-Dec14) Summary

Project Information
Project IdentifiersProject ID: 215254
DEA: 031G5104
EFIS: 0318000313
DIST-CO-RTE-PM03-BUT,COL,GLE,SUT,YOL-5,32,70,80,162-VAR
Work DescriptionREMOVE & PLACE POLYESTER CONC OVERLAY, PLACE JOINT SEAL & HMA.
Location DescriptionBUTTE, COLUSA, GLENN, SUTTER, AND YOLO COUNTIES AT VARIOUS LOCATIONS
Sample Information
Sample Taken Date3/25/2021 Sample Unique Key9
Will the laboratory/organization for which you are a member perform testing on this material sample?Yes Date that the sample was received by the laboratory/organization performing the testing3/25/2021
Sample typeQuality Control A brief description of the sample1 gallon can
The quantity of what the sample constitutes8 tankers From where was the sample collectedSource
First name of sampler or witnessed byDaniel Last name of sampler or witnessed byTikusis
Title of samplerTechnical Director Laboratory sample identification
The fabricator/manufacturer/facility nameKwik Bond Polymers and Polynt Transportation Laboratory (TL) NumberSacramento Caltrans lab
Inspector Lot Number from the Transportation Laboratory (TL) Form Structure unique identifier
Structure name
Material Information
Material TypePolyester Mfg. Lot Number(s)1322429
Batch number1322429 Mix number1322429
Test Details
DIME Sample ID: 2021-03-25-9
DIME Test ID: 2021-03-25-9-3
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2021-05-19
Test Results

Number of specimens tested: 5
Input Type: Measured
Tester's full name: Phillip Montes
Date of test: 04/06/2021
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.491 in
Sample 1 Thickness: 0.227 in
Sample 1 Area: 0.1115 in^2
Sample 1 Ultimate Strength Actual: 338 lbs
Sample 1 percent elongation: 50.6 %
Sample 1 Time: 3 MM:SS
Sample 2 Width: 0.49 in
Sample 2 Thickness: 0.228 in
Sample 2 Area: 0.1117 in^2
Sample 2 Ultimate Strength Actual: 354.4 lbs
Sample 2 percent elongation: 41.8 %
Sample 2 Time: 3 MM:SS
Sample 3 Width: 0.491 in
Sample 3 Thickness: 0.232 in
Sample 3 Area: 0.1139 in^2
Sample 3 Ultimate Strength Actual: 354.1 lbs
Sample 3 percent elongation: 54.3 %
Sample 3 Time: 3 MM:SS
Sample 4 Width: 0.49 in
Sample 4 Thickness: 0.235 in
Sample 4 Area: 0.1152 in^2
Sample 4 Ultimate Strength Actual: 364.2 lbs
Sample 4 percent elongation: 54.7 %
Sample 4 Time: 3 MM:SS
Sample 5 Width: 0.491 in
Sample 5 Thickness: 0.234 in
Sample 5 Area: 0.1149 in^2
Sample 5 Ultimate Strength Actual: 377 lbs
Sample 5 percent elongation: 68.4 %
Sample 5 Time: 3 MM:SS
Sample 1 Ultimate strength: 3031.4 psi
Sample 2 Ultimate strength : 3172.8 psi
Sample 3 Ultimate strength: 3108.9 psi
Sample 4 Ultimate strength: 3161.5 psi
Sample 5 Ultimate strength: 3281.1 psi
Ultimate Strength Average:3151 psi
Percent Elongation Average:54 %
General comments (publicly viewable) (Max 1000 characters):

Test was verified on 05/19/2021