Summary for Test 2019-05-28-4-4
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 208945 DEA: 07288604 EFIS: 0700021080 COOP: 074663 |
|---|---|
| DIST-CO-RTE-PM | 07-LA-710-6.0-9.4 |
| Award Date | 09/02/2011 |
| Closeout Date | Not set |
| Work Description | Gerald Desmond Bridge Replacement - A Design Build project. IQA samples will be selected by Port/Caltrans representatives and sent to Translab for testing. |
| Location Description | Port of Long Beach (District 7) |
| QA Service Level | 1 (Verified on 06/03/2013) |
Sample Information
| Sample Taken Date | 05/28/2019 | Sample Unique Key | 4 |
|---|---|---|---|
| Date that the sample was received by the laboratory/organization performing the testing | 05/28/2019 | Sample type | Quality Control |
| A brief description of the sample | 1 gallon can | The quantity of what the sample constitutes | 2 tankers |
| From where was the sample collected | Source | First name of sampler or witnessed by | Chris |
| Last name of sampler or witnessed by | Nunes | Title of sampler | |
| Telephone number of sampler | Laboratory sample identification | ||
| Linked DIME Sample ID | The fabricator/manufacturer/facility name | Kwik bond and Reichhold | |
| Transportation Laboratory (TL) Number | Sacramento Caltrans lab | Inspector Lot Number from the Transportation Laboratory (TL) Form | |
| Structure unique identifier | Structure name | ||
| Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | 1185836 |
|---|---|---|---|
| Batch Number | 1185836 | Mix number | 1185836 |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2019-05-28-4
DIME Test ID: 2019-05-28-4-4
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2019-06-20
Test Results
Number of specimens tested: 6
Input Type: Calculated
Tester's full name: Larry McCrum
Date of test: 06/20/2019
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.492 in
Sample 1 Thickness: 0.23 in
Sample 1 Area: 0.1131 in^2
Sample 1 Ultimate Strength Actual: 314 lbs
Sample 1 percent elongation: 48.9 %
Sample 1 Time: 3 MM:SS
Sample 2 Width: 0.491 in
Sample 2 Thickness: 0.23 in
Sample 2 Area: 0.1129 in^2
Sample 2 Ultimate Strength Actual: 333 lbs
Sample 2 percent elongation: 44.9 %
Sample 2 Time: 3 MM:SS
Sample 3 Width: 0.492 in
Sample 3 Thickness: 0.254 in
Sample 3 Area: 0.1249 in^2
Sample 3 Ultimate Strength Actual: 365.4 lbs
Sample 3 percent elongation: 57.4 %
Sample 3 Time: 4 MM:SS
Sample 4 Width: 0.492 in
Sample 4 Thickness: 0.245 in
Sample 4 Area: 0.1205 in^2
Sample 4 Ultimate Strength Actual: 353.2 lbs
Sample 4 percent elongation: 39.7 %
Sample 4 Time: 2 MM:SS
Sample 5 Width: 0.491 in
Sample 5 Thickness: 0.257 in
Sample 5 Area: 0.1261 in^2
Sample 5 Ultimate Strength Actual: 355 lbs
Sample 5 percent elongation: 47.8 %
Sample 5 Time: 3 MM:SS
Sample 6 Width: 0.492 in
Sample 6 Thickness: 0.251 in
Sample 6 Area: 0.1234 in^2
Sample 6 Ultimate Strength Actual: 322.8 lbs
Sample 6 percent elongation: 53.6 %
Sample 6 Time: 3 MM:SS
Sample 1 Ultimate strength: 2774 psi
Sample 2 Ultimate strength : 2950 psi
Sample 3 Ultimate strength: 2923 psi
Sample 4 Ultimate strength: 2931 psi
Sample 5 Ultimate strength: 2817 psi
Sample 6 Ultimate strength : 2610 psi
Ultimate Strength Average: 2834 psi
Percent Elongation Average: 48.7 %
General comments (publicly viewable) (Max 1000 characters):
Test was verified on 6/20/2019 ✔