Summary for Test 2026-09-21-30-4
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 1002398 DEA: 043Y6204 EFIS: 0423000267 |
|---|---|
| DIST-CO-RTE-PM | 04-SM-380-5.45/6.44 |
| Award Date | Not set |
| Closeout Date | Not set |
| Work Description | Not set |
| Location Description | Not set |
| QA Service Level | 1 (Verified on 07/10/2026) |
Sample Information
| Sample Taken Date | 09/21/2026 | Sample Unique Key | 30 |
|---|---|---|---|
| Date that the sample was received by the laboratory/organization performing the testing | 09/22/2026 | Sample type | Quality Control |
| A brief description of the sample | 1 gallon can / PPC 1121 RESIN | The quantity of what the sample constitutes | 10 Tankers |
| From where was the sample collected | Source | First name of sampler or witnessed by | GILBERTO |
| Last name of sampler or witnessed by | GONZALEZ | Title of sampler | Quality Manager |
| Telephone number of sampler | 9259139199 | Laboratory sample identification | 26-037 |
| Linked DIME Sample ID | The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | |
| Transportation Laboratory (TL) Number | 229KBP | Inspector Lot Number from the Transportation Laboratory (TL) Form | |
| Structure unique identifier | Structure name | ||
| Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | AZ6I01344S |
|---|---|---|---|
| Batch Number | AZ6I01344S | Mix number | AZ6I01344S |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2026-09-21-30
DIME Test ID: 2026-09-21-30-4
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2026-10-08
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Laura Bird
Date of test: 10/02/2026
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.484 in
Sample 1 Thickness: 0.261 in
Sample 1 Area: 0.1263 in^2
Sample 1 Ultimate Strength Actual: 385 lbs
Sample 1 percent elongation: 72 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.483 in
Sample 2 Thickness: 0.266 in
Sample 2 Area: 0.1285 in^2
Sample 2 Ultimate Strength Actual: 382 lbs
Sample 2 percent elongation: 70 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.483 in
Sample 3 Thickness: 0.265 in
Sample 3 Area: 0.128 in^2
Sample 3 Ultimate Strength Actual: 402 lbs
Sample 3 percent elongation: 74 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.483 in
Sample 4 Thickness: 0.262 in
Sample 4 Area: 0.1265 in^2
Sample 4 Ultimate Strength Actual: 375 lbs
Sample 4 percent elongation: 69 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.483 in
Sample 5 Thickness: 0.256 in
Sample 5 Area: 0.1236 in^2
Sample 5 Ultimate Strength Actual: 388 lbs
Sample 5 percent elongation: 74 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.483 in
Sample 6 Thickness: 0.263 in
Sample 6 Area: 0.127 in^2
Sample 6 Ultimate Strength Actual: 401 lbs
Sample 6 percent elongation: 74 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3048.3 psi
Sample 2 Ultimate strength : 2972.8 psi
Sample 3 Ultimate strength: 3140.6 psi
Sample 4 Ultimate strength: 2964.4 psi
Sample 5 Ultimate strength: 3139.2 psi
Sample 6 Ultimate strength : 3157.5 psi
Ultimate Strength Average: 3070 psi
Percent Elongation Average: 72 %
General comments (publicly viewable) (Max 1000 characters): Accepted supplier's result.
Test was verified on 10/8/2026 ✔