Summary for Test 2026-08-17-75-1
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 1001246 DEA: 041Q7214 EFIS: 0423000277 |
|---|---|
| DIST-CO-RTE-PM | 04-CC,CC,SOL-580,680,780-Var |
| Award Date | 09/25/2025 |
| Closeout Date | Not set |
| Work Description | INSTALL FIBER OPTIC CABLE SYSTEM, RAMP METERING, AND WIDEN ROADWAY. |
| Location Description | ALAMEDA, CONTRA COSTA AND SOLANO COUNTIES AT VARIOUS LOCATIONS |
| QA Service Level | 1 (Verified on 08/13/2025) |
Sample Information
| Sample Taken Date | 08/17/2026 | Sample Unique Key | 75 |
|---|---|---|---|
| Date that the sample was received by the laboratory/organization performing the testing | 08/18/2026 | Sample type | Quality Control |
| A brief description of the sample | 1 gallon can / HFST RESIN | The quantity of what the sample constitutes | 2 Tankers |
| From where was the sample collected | Source | First name of sampler or witnessed by | GILBERTO |
| Last name of sampler or witnessed by | GONZALEZ | Title of sampler | Quality Control Manager |
| Telephone number of sampler | 925-913-9199 | Laboratory sample identification | 26-030 |
| Linked DIME Sample ID | The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | |
| Transportation Laboratory (TL) Number | 223KBP | Inspector Lot Number from the Transportation Laboratory (TL) Form | |
| Structure unique identifier | Structure name | ||
| Bid Item | Not set |
Material Information
| Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | AZ6G01186 |
|---|---|---|---|
| Batch Number | AZ6G01186 | Mix Number | AZ6G01186 |
| Resin Binder Type | Polyester | Used for Overlay | Yes |
| Used for Inlay | No |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2026-08-17-75
DIME Test ID: 2026-08-17-75-1
Testing Lab: Future Labs, LLC
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2026-10-02
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Alex Hamilton
Date of test: 10/01/2026
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.2 in/min
Sample 1 Width: 0.481 in
Sample 1 Thickness: 0.122 in
Sample 1 Area: 0.0587 in^2
Sample 1 Ultimate Strength Actual: 235 lbs
Sample 1 percent elongation: 49 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.483 in
Sample 2 Thickness: 0.125 in
Sample 2 Area: 0.0604 in^2
Sample 2 Ultimate Strength Actual: 245 lbs
Sample 2 percent elongation: 52 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.48 in
Sample 3 Thickness: 0.122 in
Sample 3 Area: 0.0586 in^2
Sample 3 Ultimate Strength Actual: 223 lbs
Sample 3 percent elongation: 43 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.48 in
Sample 4 Thickness: 0.131 in
Sample 4 Area: 0.0629 in^2
Sample 4 Ultimate Strength Actual: 232 lbs
Sample 4 percent elongation: 41 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.496 in
Sample 5 Thickness: 0.129 in
Sample 5 Area: 0.064 in^2
Sample 5 Ultimate Strength Actual: 241 lbs
Sample 5 percent elongation: 47 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.494 in
Sample 6 Thickness: 0.138 in
Sample 6 Area: 0.0682 in^2
Sample 6 Ultimate Strength Actual: 245 lbs
Sample 6 percent elongation: 45 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 4003.4 psi
Sample 2 Ultimate strength : 4056.3 psi
Sample 3 Ultimate strength: 3805.5 psi
Sample 4 Ultimate strength: 3688.4 psi
Sample 5 Ultimate strength: 3765.6 psi
Sample 6 Ultimate strength : 3592.4 psi
Ultimate Strength Average: 3819 psi
Percent Elongation Average: 46 %
General comments (publicly viewable) (Max 1000 characters): Gel Time ASTM C881: 21 min.
Cure Rate ASTM D1640: 90 min.