Summary for Test 2025-09-08-33-4
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 1001124 DEA: 070W9704 EFIS: 0723000187 |
|---|---|
| DIST-CO-RTE-PM | 07-LA-10,60,71-Var |
| Award Date | 06/02/2025 |
| Closeout Date | Not set |
| Work Description | METHACRYLATE, POLYESTER OVERLAY, JOINT SEAL REPAIR, AND SPALL REPAIR. |
| Location Description | LOS ANGELES COUNTY AT VARIOUS LOCATIONS |
| QA Service Level | 1 (Verified on 08/06/2025) |
Sample Information
| Sample Taken Date | 09/08/2025 | Sample Unique Key | 33 |
|---|---|---|---|
| Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 09/09/2025 |
| Sample type | Quality Control | A brief description of the sample | 1 gallon can / PPC 1121 RESIN |
| The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
| First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
| Title of sampler | Quality Control Manager | Telephone number of sampler | 7076245467 |
| Laboratory sample identification | 000183KBP | Linked DIME Sample ID | |
| The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
| Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
| Structure name | Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | AZ5H01114 |
|---|---|---|---|
| Batch number | AZ5H01114 | Mix number | AZ5H01114 |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2025-09-08-33
DIME Test ID: 2025-09-08-33-4
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2025-09-23
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Laura Bird
Date of test: 09/11/2025
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.483 in
Sample 1 Thickness: 0.251 in
Sample 1 Area: 0.1212 in^2
Sample 1 Ultimate Strength Actual: 384 lbs
Sample 1 percent elongation: 75.4 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.483 in
Sample 2 Thickness: 0.259 in
Sample 2 Area: 0.1251 in^2
Sample 2 Ultimate Strength Actual: 344 lbs
Sample 2 percent elongation: 61.9 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.484 in
Sample 3 Thickness: 0.252 in
Sample 3 Area: 0.122 in^2
Sample 3 Ultimate Strength Actual: 406 lbs
Sample 3 percent elongation: 79.6 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.484 in
Sample 4 Thickness: 0.249 in
Sample 4 Area: 0.1205 in^2
Sample 4 Ultimate Strength Actual: 375 lbs
Sample 4 percent elongation: 73.8 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.483 in
Sample 5 Thickness: 0.256 in
Sample 5 Area: 0.1236 in^2
Sample 5 Ultimate Strength Actual: 390 lbs
Sample 5 percent elongation: 74.8 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.483 in
Sample 6 Thickness: 0.252 in
Sample 6 Area: 0.1217 in^2
Sample 6 Ultimate Strength Actual: 369 lbs
Sample 6 percent elongation: 71.7 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3168.3 psi
Sample 2 Ultimate strength : 2749.8 psi
Sample 3 Ultimate strength: 3327.9 psi
Sample 4 Ultimate strength: 3112 psi
Sample 5 Ultimate strength: 3155.3 psi
Sample 6 Ultimate strength : 3032 psi
Ultimate Strength Average: 3091 psi
Percent Elongation Average: 73 %
General comments (publicly viewable) (Max 1000 characters): Accepted supplier's result.
Test was verified on 9/23/2025 ✔