Summary for Test 2025-05-13-78-3
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 1000269 DEA: 070W6604 EFIS: 0722000360 |
|---|---|
| DIST-CO-RTE-PM | 07-LA-47,110,405,605-Var |
| Award Date | 06/25/2024 |
| Closeout Date | Not set |
| Work Description | METHACRYLATE, POLYESTER OVERLAY AND JOINT SEALS. |
| Location Description | LOS ANGELES COUNTY AT VARIOUS LOCATIONS |
| QA Service Level | 1 (Verified on 08/27/2024) |
Sample Information
| Sample Taken Date | 05/13/2025 | Sample Unique Key | 78 |
|---|---|---|---|
| Date that the sample was received by the laboratory/organization performing the testing | 06/02/2025 | Sample type | Quality Control |
| A brief description of the sample | 1 gallon can / PPC 1121 RESIN | The quantity of what the sample constitutes | 10 Tankers |
| From where was the sample collected | Source | First name of sampler or witnessed by | Gilberto |
| Last name of sampler or witnessed by | Gonzalez | Title of sampler | Quality Control Manager |
| Telephone number of sampler | 7076245467 | Laboratory sample identification | 000160KBP |
| Linked DIME Sample ID | The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | |
| Transportation Laboratory (TL) Number | 25-015 | Inspector Lot Number from the Transportation Laboratory (TL) Form | |
| Structure unique identifier | Structure name | ||
| Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | AZ5D00556S |
|---|---|---|---|
| Batch Number | AZ5D00556S | Mix number | AZ5D00556S |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2025-05-13-78
DIME Test ID: 2025-05-13-78-3
Testing Lab: Future Labs, LLC
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2025-07-24
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Alex Hamilton
Date of test: 07/11/2025
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.235 in
Sample 1 Thickness: 0.505 in
Sample 1 Area: 0.1187 in^2
Sample 1 Ultimate Strength Actual: 346 lbs
Sample 1 percent elongation: 67 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.235 in
Sample 2 Thickness: 0.509 in
Sample 2 Area: 0.1196 in^2
Sample 2 Ultimate Strength Actual: 338 lbs
Sample 2 percent elongation: 60 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.233 in
Sample 3 Thickness: 0.508 in
Sample 3 Area: 0.1184 in^2
Sample 3 Ultimate Strength Actual: 322 lbs
Sample 3 percent elongation: 59 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.242 in
Sample 4 Thickness: 0.509 in
Sample 4 Area: 0.1232 in^2
Sample 4 Ultimate Strength Actual: 352 lbs
Sample 4 percent elongation: 64 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.235 in
Sample 5 Thickness: 0.507 in
Sample 5 Area: 0.1191 in^2
Sample 5 Ultimate Strength Actual: 332 lbs
Sample 5 percent elongation: 61 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.228 in
Sample 6 Thickness: 0.509 in
Sample 6 Area: 0.1161 in^2
Sample 6 Ultimate Strength Actual: 315 lbs
Sample 6 percent elongation: 58 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 2914.9 psi
Sample 2 Ultimate strength : 2826.1 psi
Sample 3 Ultimate strength: 2719.6 psi
Sample 4 Ultimate strength: 2857.1 psi
Sample 5 Ultimate strength: 2787.6 psi
Sample 6 Ultimate strength : 2713.2 psi
Ultimate Strength Average: 2803 psi
Percent Elongation Average: 62 %
General comments (publicly viewable) (Max 1000 characters):
Test was verified on 7/24/2025 ✔