Summary for Test 2025-02-25-9-3
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 1000230 DEA: 081N2204 EFIS: 0822000120 |
|---|---|
| DIST-CO-RTE-PM | 08-SBD-66,215-Var |
| Award Date | 06/13/2024 |
| Closeout Date | 04/29/2025 |
| Work Description | FURNISH & PLACE POLYESTER CONC OVERLAY, FURNISH BR DECK TREATMENT MTL. |
| Location Description | SAN BERNARDINO COUNTY AT VARIOUS LOCATIONS |
| QA Service Level | 1 (Verified on 05/15/2024) |
Sample Information
| Sample Taken Date | 02/25/2025 | Sample Unique Key | 9 |
|---|---|---|---|
| Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 02/26/2025 |
| Sample type | Quality Control | A brief description of the sample | 1 gallon can / PPC 1121 RESIN |
| The quantity of what the sample constitutes | 9 tankers | From where was the sample collected | Source |
| First name of sampler or witnessed by | Gilberto | Last name of sampler or witnessed by | Gonzalez |
| Title of sampler | Quality Control Manager | Telephone number of sampler | 7076245467 |
| Laboratory sample identification | 000152KBP | Linked DIME Sample ID | 000152KBP |
| The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
| Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
| Structure name | Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | AZ5B00222S |
|---|---|---|---|
| Batch number | AZ5B00222S | Mix number | AZ5B000222S |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2025-02-25-9
DIME Test ID: 2025-02-25-9-3
Testing Lab: Future Labs, LLC
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2025-05-01
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Alex Hamilton
Date of test: 04/28/2025
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.509 in
Sample 1 Thickness: 0.247 in
Sample 1 Area: 0.1257 in^2
Sample 1 Ultimate Strength Actual: 378 lbs
Sample 1 percent elongation: 63 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.506 in
Sample 2 Thickness: 0.249 in
Sample 2 Area: 0.126 in^2
Sample 2 Ultimate Strength Actual: 400 lbs
Sample 2 percent elongation: 67 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.508 in
Sample 3 Thickness: 0.242 in
Sample 3 Area: 0.1229 in^2
Sample 3 Ultimate Strength Actual: 373 lbs
Sample 3 percent elongation: 64 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.509 in
Sample 4 Thickness: 0.247 in
Sample 4 Area: 0.1257 in^2
Sample 4 Ultimate Strength Actual: 351 lbs
Sample 4 percent elongation: 51 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.509 in
Sample 5 Thickness: 0.247 in
Sample 5 Area: 0.1257 in^2
Sample 5 Ultimate Strength Actual: 388 lbs
Sample 5 percent elongation: 63 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.504 in
Sample 6 Thickness: 0.248 in
Sample 6 Area: 0.125 in^2
Sample 6 Ultimate Strength Actual: 388 lbs
Sample 6 percent elongation: 65 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3007.2 psi
Sample 2 Ultimate strength : 3174.6 psi
Sample 3 Ultimate strength: 3035 psi
Sample 4 Ultimate strength: 2792.4 psi
Sample 5 Ultimate strength: 3086.7 psi
Sample 6 Ultimate strength : 3104 psi
Ultimate Strength Average: 3033 psi
Percent Elongation Average: 62 %
General comments (publicly viewable) (Max 1000 characters):
Test was verified on 5/1/2025 ✔