Summary for Test 2024-09-21-8-3
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 1000578 DEA: 112N1704 EFIS: 1122000283 |
|---|---|
| DIST-CO-RTE-PM | 11-SD-805-15.72-28.3 |
| Award Date | 05/20/2024 |
| Closeout Date | 06/09/2025 |
| Work Description | Bridge Preservation |
| Location Description | In San Diego at various locations from Landis Street Overcrossing to Sorrento Valley Boulevard Undercrossing |
| QA Service Level | 1 (Verified on 09/03/2024) |
Sample Information
| Sample Taken Date | 09/21/2024 | Sample Unique Key | 8 |
|---|---|---|---|
| Date that the sample was received by the laboratory/organization performing the testing | 09/24/2024 | Sample type | Quality Control |
| A brief description of the sample | 1 gallon can / PPC 1121 RESIN | The quantity of what the sample constitutes | 2 tankers |
| From where was the sample collected | Source | First name of sampler or witnessed by | Gilberto |
| Last name of sampler or witnessed by | Gonzalez | Title of sampler | Quality Control Manager |
| Telephone number of sampler | 7076245467 | Laboratory sample identification | 000129KBP |
| Linked DIME Sample ID | 000129KBP | The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia |
| Transportation Laboratory (TL) Number | Sacramento Caltrans lab | Inspector Lot Number from the Transportation Laboratory (TL) Form | |
| Structure unique identifier | Structure name | ||
| Bid Item | Not set |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | AZ4I01480 |
|---|---|---|---|
| Batch Number | AZ4I01480 | Mix number | AZ4I01480 |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2024-09-21-8
DIME Test ID: 2024-09-21-8-3
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2024-10-07
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 09/26/2024
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.487 in
Sample 1 Thickness: 0.255 in
Sample 1 Area: 0.1242 in^2
Sample 1 Ultimate Strength Actual: 365.521 lbs
Sample 1 percent elongation: 74.1 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.486 in
Sample 2 Thickness: 0.259 in
Sample 2 Area: 0.1259 in^2
Sample 2 Ultimate Strength Actual: 332.502 lbs
Sample 2 percent elongation: 64.9 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.485 in
Sample 3 Thickness: 0.258 in
Sample 3 Area: 0.1251 in^2
Sample 3 Ultimate Strength Actual: 303.493 lbs
Sample 3 percent elongation: 55 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.486 in
Sample 4 Thickness: 0.261 in
Sample 4 Area: 0.1268 in^2
Sample 4 Ultimate Strength Actual: 359.478 lbs
Sample 4 percent elongation: 72.8 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.486 in
Sample 5 Thickness: 0.259 in
Sample 5 Area: 0.1259 in^2
Sample 5 Ultimate Strength Actual: 328.095 lbs
Sample 5 percent elongation: 64.3 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.486 in
Sample 6 Thickness: 0.253 in
Sample 6 Area: 0.123 in^2
Sample 6 Ultimate Strength Actual: 342.432 lbs
Sample 6 percent elongation: 69.8 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 2943 psi
Sample 2 Ultimate strength : 2641 psi
Sample 3 Ultimate strength: 2426 psi
Sample 4 Ultimate strength: 2835 psi
Sample 5 Ultimate strength: 2606 psi
Sample 6 Ultimate strength : 2784 psi
Ultimate Strength Average: 2706 psi
Percent Elongation Average: 67 %
General comments (publicly viewable) (Max 1000 characters): Accepted Vendor's Results
Test was verified on 10/7/2024 ✔