DIME - Test Summary

DIME » All Projects » Project DEA: 010H1604 » Sample 2024-06-27-40 » View Test Details

Summary for Test 2024-06-27-40-2

Test performed: ASTM D638-Dec14

Project Information

Project Identifiers	Project ID: 994534 DEA: 010H1604 EFIS: 0117000117
DIST-CO-RTE-PM	01-MEN-101-R33.7/R43.2
Award Date	05/04/2023
Closeout Date	Not set
Work Description	REPLACE AC SURFACING, PLACE HMA-A, RHMA-G & CONCRETE BARRIER.
Location Description	MENDOCINO COUNTY NEAR WILLITS FROM 1.1 MILES NORTH OF WEST ROAD OVERCROSSING TO 0.6 MILE SOUTH OF HAEHL CREEK BRIDGE
QA Service Level	1 (Verified on 04/25/2023)

Sample Information

Sample Taken Date	06/27/2024	Sample Unique Key	40
Will the laboratory/organization for which you are a member perform testing on this material sample?	Yes	Date that the sample was received by the laboratory/organization performing the testing	06/28/2024
Sample type	Quality Control	A brief description of the sample	1 gallon can / HFST RESIN
The quantity of what the sample constitutes	2 tankers	From where was the sample collected	Source
First name of sampler or witnessed by	Gilberto	Last name of sampler or witnessed by	Gonzalez
Title of sampler	Quality Control Manager	Telephone number of sampler	7076245467
Laboratory sample identification	000083KBP	Linked DIME Sample ID	000083KBP
The fabricator/manufacturer/facility name	Kwik Bond Polymers, Benicia	Transportation Laboratory (TL) Number	Sacramento Caltrans lab
Inspector Lot Number from the Transportation Laboratory (TL) Form		Structure unique identifier
Structure name		Bid Item	Not set

Material Information

Material Type	High Friction Surface Treatment	Mgf. Lot Number(s)	AZ4F00945
Batch Number	AZ4F00945	Mix Number	AZ4F00945
Resin Binder Type	Polyester	Used for Overlay	Yes
Used for Inlay	No

Test Details

DIME Sample ID: 2024-06-27-40

DIME Test ID: 2024-06-27-40-2

Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory

Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics

Test Release Date: 2024-09-30

Test Results

Number of specimens tested: 6

Input Type: Measured

Tester's full name: Linda Bergstrom

Date of test: 07/08/2024

Conditioning procedure: 18/25/50+5/70

Speed of testing: 0.45 in/min

Sample 1 Width: 0.487 in

Sample 1 Thickness: 0.141 in

Sample 1 Area: 0.0687 in^2

Sample 1 Ultimate Strength Actual: 263.327 lbs

Sample 1 percent elongation: 68.5 %

Sample 1 Time: 0 MM:SS

Sample 2 Width: 0.493 in

Sample 2 Thickness: 0.136 in

Sample 2 Area: 0.067 in^2

Sample 2 Ultimate Strength Actual: 203.948 lbs

Sample 2 percent elongation: 44.8 %

Sample 2 Time: 0 MM:SS

Sample 3 Width: 0.492 in

Sample 3 Thickness: 0.141 in

Sample 3 Area: 0.0694 in^2

Sample 3 Ultimate Strength Actual: 239.985 lbs

Sample 3 percent elongation: 59.9 %

Sample 3 Time: 0 MM:SS

Sample 4 Width: 0.485 in

Sample 4 Thickness: 0.137 in

Sample 4 Area: 0.0664 in^2

Sample 4 Ultimate Strength Actual: 255.242 lbs

Sample 4 percent elongation: 68.8 %

Sample 4 Time: 0 MM:SS

Sample 5 Width: 0.486 in

Sample 5 Thickness: 0.146 in

Sample 5 Area: 0.071 in^2

Sample 5 Ultimate Strength Actual: 246.938 lbs

Sample 5 percent elongation: 60.9 %

Sample 5 Time: 0 MM:SS

Sample 6 Width: 0.488 in

Sample 6 Thickness: 0.144 in

Sample 6 Area: 0.0703 in^2

Sample 6 Ultimate Strength Actual: 251.463 lbs

Sample 6 percent elongation: 64.3 %

Sample 6 Time: 0 MM:SS

Sample 1 Ultimate strength: 3833 psi

Sample 2 Ultimate strength : 3044 psi

Sample 3 Ultimate strength: 3458 psi

Sample 4 Ultimate strength: 3844 psi

Sample 5 Ultimate strength: 3478 psi

Sample 6 Ultimate strength : 3577 psi

Ultimate Strength Average: 3539 psi

Percent Elongation Average: 61 %

General comments (publicly viewable) (Max 1000 characters): Accepted Vendor's Results: ASTM D638 Other Results: ASTM C881 Gel Time: 28 min ASTM D1640 Cure Rate 1.5 Hours

Test was verified on 9/30/2024 ✔