Summary for Test 2024-07-11-74-2
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 994889 DEA: 051M7304 EFIS: 0520000055 |
|---|---|
| DIST-CO-RTE-PM | 05-SCR-17-3.2/11.3 |
| Award Date | 08/14/2023 |
| Closeout Date | 09/02/2025 |
| Work Description | HIGH FRICTION SURFACE TREATMENT, COLD PLANE AND PLACE HMA. |
| Location Description | SANTA CRUZ COUNTY IN AND NEAR SCOTT VALLEY FROM SOUTH OF MT HERMON ROAD TO 0.6 MILE NORTH OF GLENWOOD DRIVE |
| QA Service Level | 1 (Verified on 07/24/2023) |
Sample Information
| Sample Taken Date | 07/11/2024 | Sample Unique Key | 74 |
|---|---|---|---|
| Date that the sample was received by the laboratory/organization performing the testing | 07/12/2024 | Sample type | Quality Control |
| A brief description of the sample | 1 gallon can / HFST RESIN | The quantity of what the sample constitutes | 2 tankers |
| From where was the sample collected | Source | First name of sampler or witnessed by | Gilberto |
| Last name of sampler or witnessed by | Gonzalez | Title of sampler | Quality Control Manager |
| Telephone number of sampler | 7076245467 | Laboratory sample identification | 000089KBP |
| Linked DIME Sample ID | 000089KBP | The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia |
| Transportation Laboratory (TL) Number | Sacramento Caltrans lab | Inspector Lot Number from the Transportation Laboratory (TL) Form | |
| Structure unique identifier | Structure name | ||
| Bid Item | Not set |
Material Information
| Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | AZ4F00944 |
|---|---|---|---|
| Batch Number | AZ4F00944 | Mix Number | AZ4F00944 |
| Resin Binder Type | Polyester | Used for Overlay | Yes |
| Used for Inlay | No |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2024-07-11-74
DIME Test ID: 2024-07-11-74-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2024-08-08
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 07/17/2024
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.485 in
Sample 1 Thickness: 0.135 in
Sample 1 Area: 0.0655 in^2
Sample 1 Ultimate Strength Actual: 257.219 lbs
Sample 1 percent elongation: 67.6 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.493 in
Sample 2 Thickness: 0.133 in
Sample 2 Area: 0.0656 in^2
Sample 2 Ultimate Strength Actual: 221.531 lbs
Sample 2 percent elongation: 52.1 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.486 in
Sample 3 Thickness: 0.16 in
Sample 3 Area: 0.0778 in^2
Sample 3 Ultimate Strength Actual: 270.9 lbs
Sample 3 percent elongation: 59.1 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.492 in
Sample 4 Thickness: 0.131 in
Sample 4 Area: 0.0645 in^2
Sample 4 Ultimate Strength Actual: 222.783 lbs
Sample 4 percent elongation: 55.1 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.487 in
Sample 5 Thickness: 0.14 in
Sample 5 Area: 0.0682 in^2
Sample 5 Ultimate Strength Actual: 268.026 lbs
Sample 5 percent elongation: 68.9 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.49 in
Sample 6 Thickness: 0.136 in
Sample 6 Area: 0.0666 in^2
Sample 6 Ultimate Strength Actual: 228.038 lbs
Sample 6 percent elongation: 54.3 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3927 psi
Sample 2 Ultimate strength : 3377 psi
Sample 3 Ultimate strength: 3482 psi
Sample 4 Ultimate strength: 3454 psi
Sample 5 Ultimate strength: 3930 psi
Sample 6 Ultimate strength : 3424 psi
Ultimate Strength Average: 3599 psi
Percent Elongation Average: 60 %
General comments (publicly viewable) (Max 1000 characters): ASTM 638: Accepted vendor's results ---
Gel Time ASTM C 881: 28 min ---
Cure Rate ASTM D 1640: 1.5 hrs
Test was verified on 8/8/2024 ✔