Summary for Test 2024-06-11-64-2
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 994534 DEA: 010H1604 EFIS: 0117000117 |
|---|---|
| DIST-CO-RTE-PM | 01-MEN-101-R33.7/R43.2 |
| Award Date | 05/04/2023 |
| Closeout Date | Not set |
| Work Description | REPLACE AC SURFACING, PLACE HMA-A, RHMA-G & CONCRETE BARRIER. |
| Location Description | MENDOCINO COUNTY NEAR WILLITS FROM 1.1 MILES NORTH OF WEST ROAD OVERCROSSING TO 0.6 MILE SOUTH OF HAEHL CREEK BRIDGE |
| QA Service Level | 1 (Verified on 04/25/2023) |
Sample Information
| Sample Taken Date | 06/11/2024 | Sample Unique Key | 64 |
|---|---|---|---|
| Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 06/12/2024 |
| Sample type | Quality Control | A brief description of the sample | 1 gallon can / HFST RESIN |
| The quantity of what the sample constitutes | 1 Tanker / 15 Totes | From where was the sample collected | Source |
| First name of sampler or witnessed by | GILBERTO | Last name of sampler or witnessed by | GONZALEZ |
| Title of sampler | Quality Control Manager | Telephone number of sampler | 17076245467 |
| Laboratory sample identification | 000074KBP | Linked DIME Sample ID | 000074KBP |
| The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
| Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
| Structure name | Bid Item | Not set |
Material Information
| Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | AZ4F00843 |
|---|---|---|---|
| Batch Number | AZ4F00843 | Mix Number | AZ4F00843 |
| Resin Binder Type | Polyester | Used for Overlay | Yes |
| Used for Inlay | No |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2024-06-11-64
DIME Test ID: 2024-06-11-64-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2024-07-23
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 06/14/2024
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.487 in
Sample 1 Thickness: 0.134 in
Sample 1 Area: 0.0653 in^2
Sample 1 Ultimate Strength Actual: 230.248 lbs
Sample 1 percent elongation: 51.4 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.491 in
Sample 2 Thickness: 0.135 in
Sample 2 Area: 0.0663 in^2
Sample 2 Ultimate Strength Actual: 230.326 lbs
Sample 2 percent elongation: 51.2 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.491 in
Sample 3 Thickness: 0.133 in
Sample 3 Area: 0.0653 in^2
Sample 3 Ultimate Strength Actual: 247.095 lbs
Sample 3 percent elongation: 60.6 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.49 in
Sample 4 Thickness: 0.144 in
Sample 4 Area: 0.0706 in^2
Sample 4 Ultimate Strength Actual: 265.738 lbs
Sample 4 percent elongation: 58.7 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.493 in
Sample 5 Thickness: 0.129 in
Sample 5 Area: 0.0636 in^2
Sample 5 Ultimate Strength Actual: 226.67 lbs
Sample 5 percent elongation: 39.7 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.49 in
Sample 6 Thickness: 0.141 in
Sample 6 Area: 0.0691 in^2
Sample 6 Ultimate Strength Actual: 253.528 lbs
Sample 6 percent elongation: 55 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3526 psi
Sample 2 Ultimate strength : 3474 psi
Sample 3 Ultimate strength: 3784 psi
Sample 4 Ultimate strength: 3764 psi
Sample 5 Ultimate strength: 3564 psi
Sample 6 Ultimate strength : 3669 psi
Ultimate Strength Average: 3630 psi
Percent Elongation Average: 53 %
General comments (publicly viewable) (Max 1000 characters): Gel Time ASTM C 881 = 20 min
Cure Rate ASTM D 1640 = 1 hours
Test was verified on 7/23/2024 ✔