Summary for Test 2024-05-02-34-3
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 995100 DEA: 030L2604 EFIS: 0324000072 |
---|---|
DIST-CO-RTE-PM | 03--- |
Award Date | Not set |
Closeout Date | Not set |
Work Description | Not set |
Location Description | Not set |
QA Service Level | 1 (Verified on 08/28/2023) |
Sample Information
Sample Taken Date | 05/02/2024 | Sample Unique Key | 34 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 05/03/2024 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can / 9800 RESIN |
The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | GILBERTO | Last name of sampler or witnessed by | GONZALEZ |
Title of sampler | Quality Control Manager | Telephone number of sampler | 17076245467 |
Laboratory sample identification | 000061KBP | Linked DIME Sample ID | 000061KBP |
The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Polyester | Mfg. Lot Number(s) | AZ4D00609 |
---|---|---|---|
Batch number | AZ4D00609 | Mix number | AZ4D00609 |
Test Details
DIME Sample ID: 2024-05-02-34
DIME Test ID: 2024-05-02-34-3
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2024-05-31
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 05/08/2024
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.488 in
Sample 1 Thickness: 0.263 in
Sample 1 Area: 0.1283 in^2
Sample 1 Ultimate Strength Actual: 1101 lbs
Sample 1 percent elongation: 29.9 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.488 in
Sample 2 Thickness: 0.27 in
Sample 2 Area: 0.1318 in^2
Sample 2 Ultimate Strength Actual: 1119 lbs
Sample 2 percent elongation: 32.1 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.488 in
Sample 3 Thickness: 0.265 in
Sample 3 Area: 0.1293 in^2
Sample 3 Ultimate Strength Actual: 1095 lbs
Sample 3 percent elongation: 34.4 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.489 in
Sample 4 Thickness: 0.267 in
Sample 4 Area: 0.1306 in^2
Sample 4 Ultimate Strength Actual: 1104 lbs
Sample 4 percent elongation: 22.5 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.489 in
Sample 5 Thickness: 0.263 in
Sample 5 Area: 0.1286 in^2
Sample 5 Ultimate Strength Actual: 1082 lbs
Sample 5 percent elongation: 17 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.489 in
Sample 6 Thickness: 0.261 in
Sample 6 Area: 0.1276 in^2
Sample 6 Ultimate Strength Actual: 1078 lbs
Sample 6 percent elongation: 20.4 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 8581.4 psi
Sample 2 Ultimate strength : 8490.1 psi
Sample 3 Ultimate strength: 8468.7 psi
Sample 4 Ultimate strength: 8453.3 psi
Sample 5 Ultimate strength: 8413.7 psi
Sample 6 Ultimate strength : 8448.3 psi
Ultimate Strength Average: 8476 psi
Percent Elongation Average: 26 %
General comments (publicly viewable) (Max 1000 characters): Accepted Vendor's Results
Test was verified on 5/31/2024 ✔