DIME - Test Summary

DIME » All Projects » Project DEA: 070W0404 » Sample 2023-07-06-26 » View Test Details

Summary for Test 2023-07-06-26-2

Test performed: CTM 385-November 2016

Project Information

Project Identifiers	Project ID: 993703 DEA: 070W0404 EFIS: 0721000028 MINOR: 11A3471
DIST-CO-RTE-PM	07-LA-90-0.9/T3.3
Award Date	06/09/2022
Closeout Date	02/05/2024
Work Description	PCC GRINDING, SLAB REPLACEMENT, SLURRY SEAL & COLD PLANE AC PAVEMENT.
Location Description	LOS ANGELES COUNTY IN LOS ANGELES AND CULVER CITY FROM ROUTE 1 TO SLAUSON AVENUE
QA Service Level	1 (Verified on 05/11/2022)

Sample Information

Sample Taken Date	07/06/2023	Sample Unique Key	26
Will the laboratory/organization for which you are a member perform testing on this material sample?	Yes	Date that the sample was received by the laboratory/organization performing the testing	07/11/2023
Sample type	Verification	A brief description of the sample	Scrap Crumb Rubber
The quantity of what the sample constitutes	1 Bag Crum Rubber	From where was the sample collected	Manufacturer
First name of sampler or witnessed by	Jons	Last name of sampler or witnessed by	QC
Title of sampler		Telephone number of sampler
Laboratory sample identification	0361G-23	Linked DIME Sample ID
The fabricator/manufacturer/facility name	Vulcan Materials-Irwindale	Transportation Laboratory (TL) Number
Inspector Lot Number from the Transportation Laboratory (TL) Form		Structure unique identifier
Structure name		Bid Item	Not set

Material Information

Material Type	Crumb Rubber Modifier	CRM Type	Scrap Tire
Crumb Rubber Modifier Mix Number	326120M IRW LTR

Test Details

DIME Sample ID: 2023-07-06-26

DIME Test ID: 2023-07-06-26-2

Testing Lab: CT D08 - Fontana Southern Regional Laboratory

Test Method: CTM 385-November 2016: Method of Test for Crumb Rubber Modifier (CRM)

Test Release Date: 2023-10-04

Test Results

Input Type: Measured

Tester's full name: Amir Behjati

Date of test: 07/13/2023

CRM Sample original weight: 100.0 g

Weight of talc added: 5.0 g

Accumulated weight retained No. 8: 0.0 g

Accumulated weight retained No. 10: 0.2 g

Accumulated weight retained No. 16: 36.6 g

Accumulated weight retained No. 30: 58.4 g

Accumulated weight retained No. 50: 88.9 g

Accumulated weight retained No. 100: 100.6 g

Accumulated weight retained No. 200: 102.2 g

Accumulated weight retained Pan: 103.9 g

Accumulated weight retained Total: 105.0 g

Weight of Fabric: 0.0 g

Weight of CRM: 100.0 g

Weight of Wire: 0.0 g

CRM + 0.75T: 103.8 g

CRM + T: 105.0 g

Retained Talc: 3.3 g

Retained Talc 1/3: 1.1 g

Individual weight retained No. 8: 0.0 g

Individual weight retained No. 10: 0.2 g

Individual weight retained No. 16: 36.4 g

Individual weight retained No. 30: 21.8 g

Individual weight retained No. 50: 30.5 g

Individual weight retained No. 100: 11.7 g

Individual weight retained No. 200: 1.6 g

Individual weight retained Pan: 1.7 g

Individual weight retained Total: 103.9 g

Adjusted individual weight retained No. 8: 0.0 g

Adjusted individual weight retained No. 10: 0.2 g

Adjusted individual weight retained No. 16: 35.3 g

Adjusted individual weight retained No. 30: 20.7 g

Adjusted individual weight retained No. 50: 29.4 g

Adjusted individual weight retained No. 100: 11.7 g

Adjusted individual weight retained No. 200: 1.6 g

Adjusted individual weight retained Pan: 0.0 g

Adjusted individual weight retained Total: 98.9 g

Adjusted accumulated weight retained No. 8: 0.0 g

Adjusted accumulated weight retained No. 10: 0.2 g

Adjusted accumulated weight retained No. 16: 35.5 g

Adjusted accumulated weight retained No. 30: 56.2 g

Adjusted accumulated weight retained No. 50: 85.6 g

Adjusted accumulated weight retained No. 100: 97.3 g

Adjusted accumulated weight retained No. 200: 98.9 g

Adjusted accumulated weight retained Pan: 98.9 g

Adjusted accumulated weight retained Total: 98.9 g

CRM percent retained No. 8: 0.0 %

CRM percent retained No. 10: 0.2 %

CRM percent retained No. 16: 35.9 %

CRM percent retained No. 30: 56.8 %

CRM percent retained No. 50: 86.6 %

CRM percent retained No. 100: 98.4 %

CRM percent retained No. 200: 100.0 %

CRM percent retained Pan: 100.0 %

CRM percent retained Total: 100.0 %

CRM percent passing No. 8: 100.0 %

CRM percent passing No. 10: 99.8 %

CRM percent passing No. 16: 64.1 %

CRM percent passing No. 30: 43.2 %

CRM percent passing No. 50: 13.4 %

CRM percent passing No. 100: 1.6 %

CRM percent passing No. 200: 0.0 %

CRM percent passing Pan: 0.0 %

CRM percent passing Total: 0.0 %

Fabric in CRM: 0 %

Wire in CRM: 0 %

General comments (publicly viewable) (Max 1000 characters):

Test was verified on 10/4/2023 ✔