Summary for Test 2023-05-29-1-2
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 215150 DEA: 120P0304 EFIS: 1215000024 |
|---|---|
| DIST-CO-RTE-PM | 12-ORA-74-11.5/16.6 |
| Award Date | 11/13/2020 |
| Closeout Date | 01/28/2025 |
| Work Description | PLACE HIGH FRICTION SURFACE TREATMENT, HMA & MIDWEST GUARDRAIL SYSTEM. |
| Location Description | ORANGE COUNTY NEAR SAN JUAN CAPISTRANO FROM 1.0 MILE WEST OF SAN JUAN HOT SPRINGS ROAD TO ORANGE COUNTY LINE |
| QA Service Level | 1 (Verified on 12/10/2020) |
Sample Information
| Sample Taken Date | 05/29/2023 | Sample Unique Key | 1 |
|---|---|---|---|
| Date that the sample was received by the laboratory/organization performing the testing | 05/30/2023 | Sample type | Quality Control |
| A brief description of the sample | 1 gallon can | The quantity of what the sample constitutes | 2 tankers |
| From where was the sample collected | Source | First name of sampler or witnessed by | Gilberto |
| Last name of sampler or witnessed by | Gonzalez | Title of sampler | Quality Control Manager |
| Telephone number of sampler | 17076245467 | Laboratory sample identification | 943801 |
| Linked DIME Sample ID | 943801 | The fabricator/manufacturer/facility name | Kwik Bond Polymers, Benicia |
| Transportation Laboratory (TL) Number | Sacramento Caltrans lab | Inspector Lot Number from the Transportation Laboratory (TL) Form | |
| Structure unique identifier | Structure name | ||
| Bid Item | Not set |
Material Information
| Material Type | High Friction Surface Treatment | Mgf. Lot Number(s) | 1472341 |
|---|---|---|---|
| Batch Number | 1472341 | Mix Number | 1472341 |
| Resin Binder Type | Polyester | Used for Overlay | Yes |
| Used for Inlay | No |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2023-05-29-1
DIME Test ID: 2023-05-29-1-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2023-06-29
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Linda Bergstrom
Date of test: 06/06/2023
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.15 in
Sample 1 Thickness: 0.495 in
Sample 1 Area: 0.0743 in^2
Sample 1 Ultimate Strength Actual: 249.1 lbs
Sample 1 percent elongation: 53.4 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.139 in
Sample 2 Thickness: 0.492 in
Sample 2 Area: 0.0684 in^2
Sample 2 Ultimate Strength Actual: 248.2 lbs
Sample 2 percent elongation: 60.4 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.142 in
Sample 3 Thickness: 0.493 in
Sample 3 Area: 0.07 in^2
Sample 3 Ultimate Strength Actual: 225.5 lbs
Sample 3 percent elongation: 47.7 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.135 in
Sample 4 Thickness: 0.493 in
Sample 4 Area: 0.0666 in^2
Sample 4 Ultimate Strength Actual: 257 lbs
Sample 4 percent elongation: 65.4 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.142 in
Sample 5 Thickness: 0.486 in
Sample 5 Area: 0.069 in^2
Sample 5 Ultimate Strength Actual: 218.9 lbs
Sample 5 percent elongation: 47 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.138 in
Sample 6 Thickness: 0.492 in
Sample 6 Area: 0.0679 in^2
Sample 6 Ultimate Strength Actual: 231.1 lbs
Sample 6 percent elongation: 55.2 %
Sample 6 Time: 0 MM:SS
Sample 1 Ultimate strength: 3352.6 psi
Sample 2 Ultimate strength : 3628.7 psi
Sample 3 Ultimate strength: 3221.4 psi
Sample 4 Ultimate strength: 3858.9 psi
Sample 5 Ultimate strength: 3172.5 psi
Sample 6 Ultimate strength : 3403.5 psi
Ultimate Strength Average: 3440 psi
Percent Elongation Average: 55 %
General comments (publicly viewable) (Max 1000 characters): Accepted supplier's results.
Test was verified on 6/29/2023 ✔