Summary for Test 2020-07-24-6-6
Test performed: CTM 553-1Project Information
Project Identifiers | Project ID: 214843 DEA: 060X6704 EFIS: 0618000229 |
---|---|
DIST-CO-RTE-PM | 06-TUL-63,65,99,190,198-Var |
Award Date | 05/14/2020 |
Closeout Date | 07/15/2021 |
Work Description | REPLACE BRIDGE DECK WITH POLYESTER CONCRETE OVERLAY & PLACE CONCRETE. |
Location Description | TULARE COUNTY AT VARIOUS LOCATIONS |
QA Service Level | 1 (Verified on 04/20/2020) |
Sample Information
Sample Taken Date | 07/24/2020 | Sample Unique Key | 6 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 07/24/2020 |
Sample type | Preliminary | A brief description of the sample | Rapid Setting Cement |
The quantity of what the sample constitutes | 1 Bucket | From where was the sample collected | Job Site |
First name of sampler or witnessed by | na | Last name of sampler or witnessed by | na |
Title of sampler | Telephone number of sampler | ||
Laboratory sample identification | CM204002 | Linked DIME Sample ID | |
The fabricator/manufacturer/facility name | CTS | Transportation Laboratory (TL) Number | |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Cementitious | Brand | CTS |
---|---|---|---|
Mill | Juarez | Type of Cementitious Material | Rapid Set Cement |
Test Details
DIME Sample ID: 2020-07-24-6
DIME Test ID: 2020-07-24-6-6
Testing Lab: CT HQ - Sacramento Cement Testing Laboratory
Test Method: CTM 553-1: Method for Testing Thermal Stability of Mortar Made with Hydraulic Cement
Test Release Date: 2020-08-13
Test Results
Input Type: Measured
Tester's full name: Benjamin Lenz
Date of test: 07/30/2020
Cross-sectional area of the specimen: 4 in^2
Age at the time of test: 72 hours
Maximum load at failure of specimen 1, 23 ± 1.7°C for 48h: 5880 lbs
Maximum load at failure of specimen 2, 23 ± 1.7°C for 48h: 6031 lbs
Maximum load at failure of specimen 3, 23 ± 1.7°C for 48h: 6484 lbs
Maximum load at failure of specimen 1, 50 ± 1°C for 48h: 7060 lbs
Maximum load at failure of specimen 2, 50 ± 1°C for 48h: 7548 lbs
Maximum load at failure of specimen 3, 50 ± 1°C for 48h: 7155 lbs
Average of test specimens broken to nearest 50 kPa, 23 ± 1.7°C for 48h: 10550 kPa
Average of test specimens broken to nearest 50 kPa, 50 ± 1°C for 48h: 12500 kPa
Thermal stability ratio: 118
General comments (publicly viewable) (Max 1000 characters):
Test was verified on 8/13/2020 ✔