Summary for Test 2024-06-06-123-1

Test performed: AASHTO T315-22

Project Information

Project IdentifiersProject ID: 44444
DEA: ASCP
EFIS: ASCP
DIST-CO-RTE-PM59---
Award DateNot set
Closeout DateNot set
Work DescriptionSpecial project for submitting Sample information for Asphalt Supplier Certification Program.
Location DescriptionNot set
QA Service LevelNOT VERIFIED

Sample Information

Sample Taken Date06/06/2024 Sample Unique Key123
Will the laboratory/organization for which you are a member perform testing on this material sample?Yes Date that the sample was received by the laboratory/organization performing the testing07/17/2024
Sample typeVerification A brief description of the sampleTank 40
The quantity of what the sample constitutes1 of 1 From where was the sample collectedManufacturer
First name of sampler or witnessed byKeven Last name of sampler or witnessed byHeitschmidt
Title of sampler Telephone number of sampler
Laboratory sample identificationPG64166624KF40 Linked DIME Sample ID2024-06-06-118
The fabricator/manufacturer/facility nameKlamath Falls, OR Transportation Laboratory (TL) Number
Inspector Lot Number from the Transportation Laboratory (TL) Form Structure unique identifier
Structure name

Material Information

Material TypeAsphalt Binder Performance GradePG 64-16
Modified Lot number
Sublot number Tank number
Time of sample HMA Supplier
Certified Asphalt SupplierAlbina Asphalt (Klamath Falls Plant) - Klamath Falls OR MultigradeYes
Multigrade TypePG 64-16 / PG 64-10 Asphalt Binder Mix Number

Test Details

DIME Sample ID: 2024-06-06-123
DIME Test ID: 2024-06-06-123-1
Testing Lab: CT HQ - Sacramento Asphalt Binder Laboratory
Test Method: AASHTO T315-22: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Test Release Date: 2024-07-24

Test Results


Phase: Original binder
Input Type: Measured
Tester's full name: Hamidullah Barati
Date of test: 07/23/2024
Test Gap: 1 mm
Test Frequency: 10.0 rad/s
Strain Amplitude: 12.00 %
Stress Amplitude: 0.146 kPa
Phase Angle (δ) (for the 10 cycles): 86.8 degree
Complex Modulus (G*) (for the 10 measurements): 1.207 kPa
Test Temperature (Specimen 1): 64.0 C
Dynamic Shear, G*/sin(δ): 1.21 kPa
General comments (publicly viewable) (Max 1000 characters): OG

Test was verified on 7/24/2024