Summary for Test 2022-12-05-43-1
Test performed: ASTM C109-16aProject Information
Project Identifiers | Project ID: 8801 DEA: AML-CEM EFIS: AML-CEM |
---|---|
DIST-CO-RTE-PM | 59--- |
Award Date | Not set |
Closeout Date | Not set |
Work Description | Special project for Cementitious Materials for use in Concrete Authorized Material List (AML) |
Location Description | Not set |
QA Service Level | NOT VERIFIED |
Sample Information
Sample Taken Date | 12/05/2022 | Sample Unique Key | 43 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 12/05/2022 |
Sample type | Annual Source Testing | A brief description of the sample | Slag Cement |
The quantity of what the sample constitutes | 1 Bucket | From where was the sample collected | Source |
First name of sampler or witnessed by | N/A | Last name of sampler or witnessed by | NA |
Title of sampler | Telephone number of sampler | ||
Laboratory sample identification | CM225283 | Linked DIME Sample ID | |
The fabricator/manufacturer/facility name | Nippon Slag | Transportation Laboratory (TL) Number | |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Cementitious | Brand | CalPortland |
---|---|---|---|
Mill | Nippon Steel | Type of Cementitious Material | Slag Cement |
Test Details
DIME Sample ID: 2022-12-05-43
DIME Test ID: 2022-12-05-43-1
Testing Lab: CT HQ - Sacramento Cement Testing Laboratory
Test Method: ASTM C109-16a: Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
Test Release Date: 2023-02-08
Test Results
Will control cubes be used per ASTM C311?: yes
Input Type: Measured
Tester's full name: Anthony Valdez
Date of test: 01/18/2023
Age of specimen: 7 days
The amount of flow : 104 %
The amount of water used : 47.8 %
Compressive strength of 1st specimen : 5335 psi
Compressive strength of 2nd specimen: 5063 psi
Compressive strength of 3rd specimen : 4634 psi
Average Compressive strength (to nearest 10 psi): 5200 psi
Average Compressive strength (to nearest 10 psi) control group: 4220 psi
Strength Activity Index of Portland Cement per ASTM C109: 123 %
General comments (publicly viewable) (Max 1000 characters): Specimen 3 was eliminated from the average for being outside allowable limits per Section 12 of ASTM C109
Test was verified on 2/8/2023 ✔