Summary for Test 2022-01-10-55-4

Test performed: AASHTO T313-19

Project Information

Project IdentifiersProject ID: 44444
DEA: ASCP
EFIS: ASCP
DIST-CO-RTE-PM59---
Award DateNot set
Closeout DateNot set
Work DescriptionSpecial project for submitting Sample information for Asphalt Supplier Certification Program.
Location DescriptionNot set
QA Service LevelNOT VERIFIED

Sample Information

Sample Taken Date01/10/2022 Sample Unique Key55
Will the laboratory/organization for which you are a member perform testing on this material sample?Yes Date that the sample was received by the laboratory/organization performing the testing03/01/2022
Sample typeVerification A brief description of the samplePG58-16 Asphalt binder
The quantity of what the sample constitutes2 of 2 cans split sample From where was the sample collectedManufacturer
First name of sampler or witnessed byJohn Last name of sampler or witnessed byPartenan
Title of sampler Sr Asphalt Technician Telephone number of sampler6614327352
Laboratory sample identification5816220110 Linked DIME Sample ID2022-01-10-51
The fabricator/manufacturer/facility nameSan Joaquin Refinery, Bakersfield, CA Transportation Laboratory (TL) Number
Inspector Lot Number from the Transportation Laboratory (TL) Form Structure unique identifier
Structure name

Material Information

Material TypeAsphalt Binder Performance GradePG 58-16
ModifiedNo Lot number5816220110
Sublot number Tank number2002
Time of sample8:20 am HMA Supplier
Certified Asphalt SupplierSan Joaquin Refinery - Bakersfield CA MultigradeNo
Multigrade Type Asphalt Binder Mix NumberNot set

Test Details

DIME Sample ID: 2022-01-10-55
DIME Test ID: 2022-01-10-55-4
Testing Lab: CT HQ - Sacramento Asphalt Binder Laboratory
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Test Release Date: 2022-03-04

Test Results


Input Type: Measured
Tester's full name: Ruben Macias
Date of test: 03/02/2022
Minimum test bath temperature at 240 s: -6.0 C
Maximum test bath temperature at 240 s: -6.0 C
Time of test load application: no data
File name of test data: no data
Time beam in bath: no data
Time test started: no data
Flags issued by software during test: no data
Correlation coefficient (R²): 0
Regression coefficient a: no data
Regression coefficient b: no data
Regression coefficient c: no data
Load at time 0.0: 0.0 mN
Deflection at time 0.0 s: 0.000 µm
Load at time 0.5 s: 0.0 mN
Deflection at time 0.5 s: 0.000 µm
Load at 60.0 s: 965.0 mN
Beam deflection 60.0 s: 0.926 µm
Measured Stiffness Modulus 60.0 s: 84.000 mPa
Estimated Stiffness Modulus 60.0 s: 84.000 mPa
Difference between stiffness moduli 60.0 s: no data
Estimated m-value 60.0 s: 0.473
General comments (publicly viewable) (Max 1000 characters):

Test was verified on 3/4/2022