Summary for Test 2021-11-02-15-2
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 215707 DEA: 030J9004 EFIS: 0320000039 |
---|---|
DIST-CO-RTE-PM | 03-BUT,PLA,SAC-50,51,80,99-VAR |
Award Date | 06/09/2021 |
Closeout Date | 07/25/2022 |
Work Description | PLACE HMA AND APPLY HIGH FRICTION SURFACE TREATMENT. |
Location Description | BUTTE, PLACER, AND SACRAMENTO COUNTIES AT VARIOUS LOCATIONS |
QA Service Level | 1 (Verified on 05/20/2021) |
Sample Information
Sample Taken Date | 11/02/2021 | Sample Unique Key | 15 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 11/02/2021 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | Daniel | Last name of sampler or witnessed by | Tikusis |
Title of sampler | Technical Director | Telephone number of sampler | 7073309227 |
Laboratory sample identification | Linked DIME Sample ID | ||
The fabricator/manufacturer/facility name | Kwik Bond Polymers and Polynt | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Polyester | Mfg. Lot Number(s) | 1368339 |
---|---|---|---|
Batch number | 1368339 | Mix number | 1368339 |
Test Details
DIME Sample ID: 2021-11-02-15
DIME Test ID: 2021-11-02-15-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2021-11-15
Test Results
Number of specimens tested: 5
Input Type: Measured
Tester's full name: Vendors Results
Date of test: 11/15/2021
Conditioning procedure: 40/25
Speed of testing: 0.45 in/min
Sample 1 Width: 0.5 in
Sample 1 Thickness: 0.128 in
Sample 1 Area: 0.064 in^2
Sample 1 Ultimate Strength Actual: 268.531 lbs
Sample 1 percent elongation: 58 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.5 in
Sample 2 Thickness: 0.128 in
Sample 2 Area: 0.064 in^2
Sample 2 Ultimate Strength Actual: 253.997 lbs
Sample 2 percent elongation: 49.1 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.5 in
Sample 3 Thickness: 0.129 in
Sample 3 Area: 0.0645 in^2
Sample 3 Ultimate Strength Actual: 250.67 lbs
Sample 3 percent elongation: 37 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.5 in
Sample 4 Thickness: 0.127 in
Sample 4 Area: 0.0635 in^2
Sample 4 Ultimate Strength Actual: 270.516 lbs
Sample 4 percent elongation: 60.4 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.5 in
Sample 5 Thickness: 0.125 in
Sample 5 Area: 0.0625 in^2
Sample 5 Ultimate Strength Actual: 261.79 lbs
Sample 5 percent elongation: 59.7 %
Sample 5 Time: 0 MM:SS
Sample 1 Ultimate strength: 4195.8 psi
Sample 2 Ultimate strength : 3968.7 psi
Sample 3 Ultimate strength: 3886.4 psi
Sample 4 Ultimate strength: 4260.1 psi
Sample 5 Ultimate strength: 4188.6 psi
Ultimate Strength Average: 4100 psi
Percent Elongation Average: 53 %
General comments (publicly viewable) (Max 1000 characters): Accepted Based On Supplier Results
Test was verified on 11/15/2021 ✔