Summary for Test 2021-10-19-4-3

Test performed: ASTM D638-Dec14

Project Information

Project IdentifiersProject ID: 215621
DEA: 010J8704
EFIS: 0119000117
DIST-CO-RTE-PM01-MEN-101,271-VAR
Award Date05/14/2021
Closeout Date10/20/2022
Work DescriptionPLACE HMA, POLYESTER CONCRETE OVERLAY AND COLD PLANE.
Location DescriptionMENDOCINO COUNTY AT VARIOUS LOCATIONS
QA Service Level1 (Verified on 04/07/2021)

Sample Information

Sample Taken Date10/19/2021 Sample Unique Key4
Will the laboratory/organization for which you are a member perform testing on this material sample?Yes Date that the sample was received by the laboratory/organization performing the testing10/19/2021
Sample typeQuality Control A brief description of the sample1 gallon can
The quantity of what the sample constitutes2 tankers From where was the sample collectedSource
First name of sampler or witnessed byDaniel Last name of sampler or witnessed byTikusis
Title of samplerTechnical Director Telephone number of sampler707-330-9227
Laboratory sample identification Linked DIME Sample ID
The fabricator/manufacturer/facility nameKwik Bond Polymers and Polynt Transportation Laboratory (TL) NumberSacramento Caltrans lab
Inspector Lot Number from the Transportation Laboratory (TL) Form Structure unique identifier
Structure name

Material Information

Material TypePolyester Mfg. Lot Number(s)1366420
Batch number1366420 Mix number1366420

Test Details

DIME Sample ID: 2021-10-19-4
DIME Test ID: 2021-10-19-4-3
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2021-10-29

Test Results


Number of specimens tested: 5
Input Type: Measured
Tester's full name: Vendor Results
Date of test: 10/29/2021
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.486 in
Sample 1 Thickness: 0.256 in
Sample 1 Area: 0.1244 in^2
Sample 1 Ultimate Strength Actual: 412.96 lbs
Sample 1 percent elongation: 66.11 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.488 in
Sample 2 Thickness: 0.258 in
Sample 2 Area: 0.1259 in^2
Sample 2 Ultimate Strength Actual: 408.26 lbs
Sample 2 percent elongation: 64.29 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.486 in
Sample 3 Thickness: 0.247 in
Sample 3 Area: 0.12 in^2
Sample 3 Ultimate Strength Actual: 407.4 lbs
Sample 3 percent elongation: 66.24 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.487 in
Sample 4 Thickness: 0.25 in
Sample 4 Area: 0.1218 in^2
Sample 4 Ultimate Strength Actual: 386.46 lbs
Sample 4 percent elongation: 60.13 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.487 in
Sample 5 Thickness: 0.253 in
Sample 5 Area: 0.1232 in^2
Sample 5 Ultimate Strength Actual: 433.8 lbs
Sample 5 percent elongation: 69.45 %
Sample 5 Time: 0 MM:SS
Sample 1 Ultimate strength: 3319.6 psi
Sample 2 Ultimate strength : 3242.7 psi
Sample 3 Ultimate strength: 3395 psi
Sample 4 Ultimate strength: 3172.9 psi
Sample 5 Ultimate strength: 3521.1 psi
Ultimate Strength Average: 3330 psi
Percent Elongation Average: 65 %
General comments (publicly viewable) (Max 1000 characters): Accepted Based On Supplier Results

Test was verified on 10/29/2021