Summary for Test 2020-11-11-9-2
Test performed: ASTM D638-Dec14Project Information
| Project Identifiers | Project ID: 214908 DEA: 112N0424 EFIS: 1118000193 |
|---|---|
| DIST-CO-RTE-PM | 11-SD-76-R4.2/R6.4 |
| Award Date | 06/09/2020 |
| Closeout Date | 01/31/2022 |
| Work Description | PLACE MICROSURFACING, COLD PLANE AND REPLACE AC WITH HOT MIX ASPHALT. |
| Location Description | SAN DIEGO COUNTY IN OCEANSIDE FROM RANCHO DEL ORO DRIVE TO 0.2 MILE EAST OF COLLEGE BOULEVARD |
| QA Service Level | 1 (Verified on 09/15/2020) |
Sample Information
| Sample Taken Date | 11/11/2020 | Sample Unique Key | 9 |
|---|---|---|---|
| Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 11/11/2020 |
| Sample type | Quality Control | A brief description of the sample | 1 gallon can |
| The quantity of what the sample constitutes | 1 Tanker 16 Totes | From where was the sample collected | Source |
| First name of sampler or witnessed by | Daniel | Last name of sampler or witnessed by | Tikusis |
| Title of sampler | Technical Director | Telephone number of sampler | 707-330-9227 |
| Laboratory sample identification | Linked DIME Sample ID | ||
| The fabricator/manufacturer/facility name | Kwik Bond Polymers and Polynt | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
| Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
| Structure name |
Material Information
| Material Type | Polyester | Mfg. Lot Number(s) | 112N0424 |
|---|---|---|---|
| Batch number | 112N0424 | Mix number | 112N0424 |
Test Details
Test Details QR Code
Scan this code to open this Test Details view on another device.
Sample Details QR Code
Scan this code to open this Sample Details view on another device.
DIME Sample ID: 2020-11-11-9
DIME Test ID: 2020-11-11-9-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2020-12-04
Test Results
Number of specimens tested: 5
Input Type: Measured
Tester's full name: Vendor results
Date of test: 12/04/2020
Conditioning procedure: 40/25/50
Speed of testing: 0.45 in/min
Sample 1 Width: 0.491 in
Sample 1 Thickness: 0.146 in
Sample 1 Area: 0.0717 in^2
Sample 1 Ultimate Strength Actual: 267.9 lbs
Sample 1 percent elongation: 66.7 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.49 in
Sample 2 Thickness: 0.147 in
Sample 2 Area: 0.072 in^2
Sample 2 Ultimate Strength Actual: 230 lbs
Sample 2 percent elongation: 53.6 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.49 in
Sample 3 Thickness: 0.153 in
Sample 3 Area: 0.075 in^2
Sample 3 Ultimate Strength Actual: 244.5 lbs
Sample 3 percent elongation: 56.6 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.493 in
Sample 4 Thickness: 0.149 in
Sample 4 Area: 0.0735 in^2
Sample 4 Ultimate Strength Actual: 232.5 lbs
Sample 4 percent elongation: 52.5 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.49 in
Sample 5 Thickness: 0.138 in
Sample 5 Area: 0.0676 in^2
Sample 5 Ultimate Strength Actual: 255.6 lbs
Sample 5 percent elongation: 64.2 %
Sample 5 Time: 0 MM:SS
Sample 1 Ultimate strength: 3736.4 psi
Sample 2 Ultimate strength : 3194.4 psi
Sample 3 Ultimate strength: 3260 psi
Sample 4 Ultimate strength: 3163.3 psi
Sample 5 Ultimate strength: 3781.1 psi
Ultimate Strength Average: 3427 psi
Percent Elongation Average: 59 %
General comments (publicly viewable) (Max 1000 characters): Accepted supplier's results.
Test was verified on 12/4/2020 ✔