Summary for Test 2020-02-25-2-4
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 213977 DEA: 081J1404 EFIS: 0817000214 |
---|---|
DIST-CO-RTE-PM | 08--,40&58- |
Award Date | 05/01/2019 |
Closeout Date | 09/02/2020 |
Work Description | Not set |
Location Description | Not set |
QA Service Level | 1 (Verified on 06/07/2019) |
Sample Information
Sample Taken Date | 02/25/2020 | Sample Unique Key | 2 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 02/25/2020 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | Daniel | Last name of sampler or witnessed by | Tikusis |
Title of sampler | Technical Director | Telephone number of sampler | |
Laboratory sample identification | Linked DIME Sample ID | ||
The fabricator/manufacturer/facility name | Kwik Bond Polymers and Reichhold | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Polyester | Mfg. Lot Number(s) | 1234812 |
---|---|---|---|
Batch number | 1234812 | Mix number | 1234812 |
Test Details
DIME Sample ID: 2020-02-25-2
DIME Test ID: 2020-02-25-2-4
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2020-03-25
Test Results
Number of specimens tested: 6
Input Type: Measured
Tester's full name: Phillip Montes
Date of test: 03/25/2020
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.48 in
Sample 1 Thickness: 0.26 in
Sample 1 Area: 0.1248 in^2
Sample 1 Ultimate Strength Actual: 397.3 lbs
Sample 1 percent elongation: 51.8 %
Sample 1 Time: 3 MM:SS
Sample 2 Width: 0.481 in
Sample 2 Thickness: 0.27 in
Sample 2 Area: 0.1299 in^2
Sample 2 Ultimate Strength Actual: 405.5 lbs
Sample 2 percent elongation: 58.3 %
Sample 2 Time: 3 MM:SS
Sample 3 Width: 0.482 in
Sample 3 Thickness: 0.259 in
Sample 3 Area: 0.1248 in^2
Sample 3 Ultimate Strength Actual: 388.9 lbs
Sample 3 percent elongation: 58.6 %
Sample 3 Time: 4 MM:SS
Sample 4 Width: 0.483 in
Sample 4 Thickness: 0.258 in
Sample 4 Area: 0.1246 in^2
Sample 4 Ultimate Strength Actual: 377.2 lbs
Sample 4 percent elongation: 46.6 %
Sample 4 Time: 3 MM:SS
Sample 5 Width: 0.482 in
Sample 5 Thickness: 0.267 in
Sample 5 Area: 0.1287 in^2
Sample 5 Ultimate Strength Actual: 375.4 lbs
Sample 5 percent elongation: 50.1 %
Sample 5 Time: 0 MM:SS
Sample 6 Width: 0.482 in
Sample 6 Thickness: 0.267 in
Sample 6 Area: 0.1287 in^2
Sample 6 Ultimate Strength Actual: 383.8 lbs
Sample 6 percent elongation: 53.1 %
Sample 6 Time: 3 MM:SS
Sample 1 Ultimate strength: 3183.5 psi
Sample 2 Ultimate strength : 3121.6 psi
Sample 3 Ultimate strength: 3116.2 psi
Sample 4 Ultimate strength: 3027.3 psi
Sample 5 Ultimate strength: 2916.9 psi
Sample 6 Ultimate strength : 2982.1 psi
Ultimate Strength Average: 3058 psi
Percent Elongation Average: 53 %
General comments (publicly viewable) (Max 1000 characters):
Test was verified on 3/25/2020 ✔