Summary for Test 2018-05-09-5-4
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 213022 DEA: 010G3504 EFIS: 0116000173 |
---|---|
DIST-CO-RTE-PM | 01-HUM-101-68.2/R93.0 |
Award Date | 03/06/2018 |
Closeout Date | 11/27/2018 |
Work Description | POLYESTER CONCRETE OVERLAY & METHACRYLATE DECK TREATMENT |
Location Description | HUMBOLDT COUNTY AT VARIOUS LOCATIONS |
QA Service Level | 1 (Verified on 04/27/2018) |
Sample Information
Sample Taken Date | 05/09/2018 | Sample Unique Key | 5 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 05/09/2018 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 10 Tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | Chris | Last name of sampler or witnessed by | Nunes |
Title of sampler | Unknown | Telephone number of sampler | Unknown |
Laboratory sample identification | Unknown | Linked DIME Sample ID | Unknown |
The fabricator/manufacturer/facility name | Kwik bond and Reichhold | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Unknown | Structure unique identifier | Not set |
Structure name | Not set |
Material Information
Material Type | Polyester | Mfg. Lot Number(s) | 1119488 |
---|---|---|---|
Batch number | 1119488 | Mix number | 1119488 |
Test Details
DIME Sample ID: 2018-05-09-5
DIME Test ID: 2018-05-09-5-4
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2018-07-27
Test Results
Number of specimens tested: 4
Input Type: Calculated
Tester's full name: Mike Mullins
Date of test: 07/27/2018
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.493 in
Sample 1 Thickness: 0.246 in
Sample 1 Area: 0.1213 in^2
Sample 1 Ultimate Strength Actual: 2896 lbs
Sample 1 percent elongation: 59.3 %
Sample 1 Time: 4.17 MM:SS
Sample 2 Width: 0.492 in
Sample 2 Thickness: 0.244 in
Sample 2 Area: 1200 in^2
Sample 2 Ultimate Strength Actual: 3249 lbs
Sample 2 percent elongation: 66.4 %
Sample 2 Time: 5.09 MM:SS
Sample 3 Width: 0.492 in
Sample 3 Thickness: 0.25 in
Sample 3 Area: 0.123 in^2
Sample 3 Ultimate Strength Actual: 2952 lbs
Sample 3 percent elongation: 58.8 %
Sample 3 Time: 4.27 MM:SS
Sample 4 Width: 0.492 in
Sample 4 Thickness: 0.25 in
Sample 4 Area: 0.123 in^2
Sample 4 Ultimate Strength Actual: 2716 lbs
Sample 4 percent elongation: 41.9 %
Sample 4 Time: 2.52 MM:SS
Sample 1 Ultimate strength: 2896 psi
Sample 2 Ultimate strength : 3249 psi
Sample 3 Ultimate strength: 2952 psi
Sample 4 Ultimate strength: 2716 psi
Ultimate Strength Average: 2955 psi
Percent Elongation Average: 56.4 %
General comments (publicly viewable) (Max 1000 characters):
Test was verified on 7/27/2018 ✔