Test 2016-02-06-1-2 (ASTM C109-11) Summary

Project Information
Project IdentifiersProject ID: 88888
Work DescriptionSpecial project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location DescriptionNot set
Sample Information
Sample Taken Date2/6/2016 Sample Unique Key1
Will the laboratory/organization for which you are a member perform testing on this material sample?Yes Date that the sample was received by the laboratory/organization performing the testing8/4/2016
Sample typeAnnual Source Testing A brief description of the sampletype II/V
The quantity of what the sample constitutes1 Bucket From where was the sample collectedSource
First name of sampler or witnessed byUnknown Last name of sampler or witnessed byUnknown
Title of samplerUnknown Laboratory sample identificationCM165629
The fabricator/manufacturer/facility nameCal portland Transportation Laboratory (TL) NumberUnknown
Inspector Lot Number from the Transportation Laboratory (TL) FormUnknown Structure unique identifierNot set
Structure nameNot set
Material Information
Material TypeCementitious BrandRillito
MillCal Portland Type of Cementitious MaterialType II/V Cement
Test Details
DIME Sample ID: 2016-02-06-1
DIME Test ID: 2016-02-06-1-2
Testing Lab: CT HQ - Sacramento Cement Testing Laboratory
Test Method: ASTM C109-11: Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50mm] Cube Specimens)
Test Release Date: 2019-03-27
Test Results

Will control cubes be used per ASTM C311?: no
Input Type: Measured
Tester's full name: Stephen Donnelly
Date of test: 08/23/2016
Age of specimen: 199 days
The amount of flow (In percent): 110 %
The amount of water used (In percent): 49 %
Maximum load of 1st specimen (lb): 20272 lb
Maximum load of 2nd specimen (lb): 20752 lb
Maximum load of 3rd specimen (lb): 19510 lb
Cross sectional area loaded of 1st specimen (sq. inch): 4 in^2
Cross sectional area loaded of 2nd specimen (sq. inch): 4 in^2
Cross sectional area loaded of 3rd specimen (sq. inch): 4 in^2
Compressive strength of 1st specimen (psi): 5068 psi
Compressive strength of 2nd specimen (psi): 5188 psi
Compressive strength of 3rd specimen (psi): 4877.5 psi
Average Compressive strength (to nearest 10 psi): 5040 psi
General comments (publicly viewable) (Max 1000 characters): CM 165629 7 day break

Test was verified on 03/20/2019