Summary for Test 2021-01-11-3-2
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 215267 DEA: 041W3804 EFIS: 0421000007 |
---|---|
DIST-CO-RTE-PM | 04-MRN-101-.4/2.2, 12.82, 14.62 |
Award Date | 10/29/2020 |
Closeout Date | 12/16/2021 |
Work Description | Not set |
Location Description | Not set |
QA Service Level | 1 (Verified on 11/09/2020) |
Sample Information
Sample Taken Date | 01/11/2021 | Sample Unique Key | 3 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 01/15/2021 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 32 Totes | From where was the sample collected | Source |
First name of sampler or witnessed by | Daniel | Last name of sampler or witnessed by | Tikusis |
Title of sampler | Technical Director | Telephone number of sampler | 707-330-9227 |
Laboratory sample identification | Linked DIME Sample ID | ||
The fabricator/manufacturer/facility name | Kwik Bond Polymers and Polynt | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Polyester | Mfg. Lot Number(s) | 1304790 |
---|---|---|---|
Batch number | 1304790 | Mix number | 1304790 |
Test Details
DIME Sample ID: 2021-01-11-3
DIME Test ID: 2021-01-11-3-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2021-01-28
Test Results
Number of specimens tested: 5
Input Type: Measured
Tester's full name: Vendor results
Date of test: 01/28/2021
Conditioning procedure: 40/25/50
Speed of testing: 0.2 in/min
Sample 1 Width: 0.488 in
Sample 1 Thickness: 0.155 in
Sample 1 Area: 0.0756 in^2
Sample 1 Ultimate Strength Actual: 278.3 lbs
Sample 1 percent elongation: 65.08 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.493 in
Sample 2 Thickness: 0.152 in
Sample 2 Area: 0.0749 in^2
Sample 2 Ultimate Strength Actual: 263.6 lbs
Sample 2 percent elongation: 61.66 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.493 in
Sample 3 Thickness: 0.147 in
Sample 3 Area: 0.0725 in^2
Sample 3 Ultimate Strength Actual: 263.9 lbs
Sample 3 percent elongation: 64.27 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.491 in
Sample 4 Thickness: 0.146 in
Sample 4 Area: 0.0717 in^2
Sample 4 Ultimate Strength Actual: 235.7 lbs
Sample 4 percent elongation: 55.08 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.492 in
Sample 5 Thickness: 0.152 in
Sample 5 Area: 0.0748 in^2
Sample 5 Ultimate Strength Actual: 265.1 lbs
Sample 5 percent elongation: 61.79 %
Sample 5 Time: 0 MM:SS
Sample 1 Ultimate strength: 3681.2 psi
Sample 2 Ultimate strength : 3519.4 psi
Sample 3 Ultimate strength: 3640 psi
Sample 4 Ultimate strength: 3287.3 psi
Sample 5 Ultimate strength: 3544.1 psi
Ultimate Strength Average: 3534 psi
Percent Elongation Average: 62 %
General comments (publicly viewable) (Max 1000 characters): Accepted vendor results
Test was verified on 1/28/2021 ✔