Summary for Test 2020-12-04-3-2
Test performed: ASTM D638-Dec14Project Information
Project Identifiers | Project ID: 215267 DEA: 041W3804 EFIS: 0421000007 |
---|---|
DIST-CO-RTE-PM | 04-MRN-101-.4/2.2, 12.82, 14.62 |
Award Date | 10/29/2020 |
Closeout Date | 12/16/2021 |
Work Description | Not set |
Location Description | Not set |
QA Service Level | 1 (Verified on 11/09/2020) |
Sample Information
Sample Taken Date | 12/04/2020 | Sample Unique Key | 3 |
---|---|---|---|
Will the laboratory/organization for which you are a member perform testing on this material sample? | Yes | Date that the sample was received by the laboratory/organization performing the testing | 12/04/2020 |
Sample type | Quality Control | A brief description of the sample | 1 gallon can |
The quantity of what the sample constitutes | 2 tankers | From where was the sample collected | Source |
First name of sampler or witnessed by | Daniel | Last name of sampler or witnessed by | Tikusis |
Title of sampler | Technical Director | Telephone number of sampler | 707-330-9227 |
Laboratory sample identification | Linked DIME Sample ID | ||
The fabricator/manufacturer/facility name | Kwik Bond Polymers and Polynt | Transportation Laboratory (TL) Number | Sacramento Caltrans lab |
Inspector Lot Number from the Transportation Laboratory (TL) Form | Structure unique identifier | ||
Structure name |
Material Information
Material Type | Polyester | Mfg. Lot Number(s) | 1294701 |
---|---|---|---|
Batch number | 1294701 | Mix number | 1294701 |
Test Details
DIME Sample ID: 2020-12-04-3
DIME Test ID: 2020-12-04-3-2
Testing Lab: CT HQ - Sacramento Concrete Testing Laboratory
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Test Release Date: 2020-12-24
Test Results
Number of specimens tested: 5
Input Type: Measured
Tester's full name: Phillip Montes
Date of test: 12/24/2020
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.5 in
Sample 1 Thickness: 0.135 in
Sample 1 Area: 0.0675 in^2
Sample 1 Ultimate Strength Actual: 267.264 lbs
Sample 1 percent elongation: 44.8 %
Sample 1 Time: 0 MM:SS
Sample 2 Width: 0.5 in
Sample 2 Thickness: 0.128 in
Sample 2 Area: 0.064 in^2
Sample 2 Ultimate Strength Actual: 264.067 lbs
Sample 2 percent elongation: 44.7 %
Sample 2 Time: 0 MM:SS
Sample 3 Width: 0.5 in
Sample 3 Thickness: 0.137 in
Sample 3 Area: 0.0685 in^2
Sample 3 Ultimate Strength Actual: 274.75 lbs
Sample 3 percent elongation: 50.6 %
Sample 3 Time: 0 MM:SS
Sample 4 Width: 0.5 in
Sample 4 Thickness: 0.133 in
Sample 4 Area: 0.0665 in^2
Sample 4 Ultimate Strength Actual: 266.011 lbs
Sample 4 percent elongation: 40 %
Sample 4 Time: 0 MM:SS
Sample 5 Width: 0.5 in
Sample 5 Thickness: 0.138 in
Sample 5 Area: 0.069 in^2
Sample 5 Ultimate Strength Actual: 286.19 lbs
Sample 5 percent elongation: 33.7 %
Sample 5 Time: 0 MM:SS
Sample 1 Ultimate strength: 3959.5 psi
Sample 2 Ultimate strength : 4126 psi
Sample 3 Ultimate strength: 4010.9 psi
Sample 4 Ultimate strength: 4000.2 psi
Sample 5 Ultimate strength: 4147.7 psi
Ultimate Strength Average: 4049 psi
Percent Elongation Average: 43 %
General comments (publicly viewable) (Max 1000 characters): Accepted vendor results
Test was verified on 12/24/2020 ✔