Print Report | Back to Test Summary

Testing Report for 2020-11-09-15-5

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: STOCK
EFIS: STOCK
Project ID: 88888
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-11-09-15
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM2 - Type B Elastomeric Joint Seal
Sample Taken Date: 11/9/2020
Date that the sample was received by the laboratory/organization performing the testing: 11/13/2020
The quantity of what the sample constitutes: 600'
A brief description of the sample: joint seal
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Watson Bowman

Material Information

Mfg. Lot Number(s): 2920401
Manufacturer(s): Watson Bowman
Temperature: 72
Humidity: 50
Comments:
Joint Seal Size: 5"

Test Information

DIME Test ID: 2020-11-09-15-5
Test Method: ASTM D2628-91-re16: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements
Date Tested: 11/20/2020
Verified Date: 12/16/2020
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified :

Submitted Test Results

High or low tempurature: High
Temperature: 72 f
Humidity: 50 %
Temp Recovery (22 hrs at -20F) Size Before (Height of Contact Face ): 5 in
Temp Recovery (22 hrs at -20F) Size After (Recovered Contact Face ): 4.9165 in
Percent Recovery: 98 %