Testing Report for 2020-06-29-6-1

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 051M5004
EFIS: 0519000166
Project ID: 214732
QA Service Level: 1
DIST-CO-RTE-PM: 05-SB-166-0.2/6.9
Work Description: COLD PLANE EXISTING ROADWAY AND PLACE RHMA-G.
Location Description: SANTA BARBARA COUNTY IN AND NEAR GUADALUPE AND SANTA MARIA FROM OBISPO STREET TO BLOSSER ROAD
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Thomas Peterson
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-06-29-6
TL Number from the TL Form:
Sample Submitted By Organization: CT D05 - Field Laboratory
Sample Organization Contact: (559) 230-3109
Type of Sample: Acceptance
Type of Material: Hot Mix Asphalt
Sample Taken Date: 6/29/2020
Date that the sample was received by the laboratory/organization performing the testing: 6/30/2020
The quantity of what the sample constitutes: 1 box
A brief description of the sample: 1/2" RHMA-G
From where was the sample collected: Manufacturer
Laboratory sample identification: 20-A-120
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: CalPortland Garey Hot Plant

Material Information

HMA Type: RHMA-G
HMA Grading: 1/2 inch
Lot number: 1
Sublot number: 15

Test Information

DIME Test ID: 2020-06-29-6-1
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Asphalt Binder Content)
Date Tested: 6/30/2020
Verified Date: 6/30/2020
Submitted By Organization: CT D05 - Field Laboratory
Organization Address: 50 Higuera St,
Organization City: San Luis Obispo
Organization State: CA
Organization Zipcode: 93401
Organization Email: doug.lambert@dot.ca.gov
Organization Phone: (559) 230-3109
General Comments for this Test:
Test Result Compliance: does not comply
Additional Comments When Verified :

Submitted Test Results

Asphalt Binder Content: 6.82 %
Correction Factor (Percent by mass of HMA Specimen): no data