Print Report | Back to Test Summary

Testing Report for 2020-01-30-17-5

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 051M2404
EFIS: 0519000085
Project ID: 214634
QA Service Level: 1
DIST-CO-RTE-PM: 05-SB-101-21.8/22.0
Work Description: Goleta Cross Slope Correction
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Kevin Murdock
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-01-30-17
TL Number from the TL Form:
Sample Submitted By Organization: CT D05 - Field Laboratory
Sample Organization Contact: (559) 230-3109
Type of Sample: Verification
Type of Material: Hot Mix Asphalt
Sample Taken Date: 1/30/2020
Date that the sample was received by the laboratory/organization performing the testing: 1/31/2020
The quantity of what the sample constitutes: Verification Testing
A brief description of the sample: 12 x 20 lbs boxes
From where was the sample collected: Manufacturer
Laboratory sample identification: D5 20-J-001
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: CalPortland Garey

Material Information

HMA Type: Type A HMA
HMA Grading: 3/4 inch
Lot number: Unknown
Sublot number: Unknown

Test Information

DIME Test ID: 2020-01-30-17-5
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Asphalt Binder Content)
Date Tested: 2/18/2020
Verified Date: 2/18/2020
Submitted By Organization: CT D05 - Field Laboratory
Organization Address: 50 Higuera St,
Organization City: San Luis Obispo
Organization State: CA
Organization Zipcode: 93401
Organization Email: doug.lambert@dot.ca.gov
Organization Phone: (559) 230-3109
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Test procedure used?: Method A
Asphalt Binder Content: 5.27 %
Mass of HMA prior to ignition: 2276.5 g
Mass of aggregate remaining after ignition: 2133.6 g
Correction Factor (Percent by mass of HMA Specimen): 1.01 %
Moisture Content: no data
Test Temperature: 899.6 F