Print Report | Back to Sample Detail

Sample Record for 2020-01-14-2

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 8801 DEA: AML-CEM EFIS: AML-CEM QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for Cementitious Materials for use in Concrete Authorized Material List (AML)
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-01-14-2
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Sample Organization Contact: (916) 227-7071
Type of Sample: Annual Source Testing
Type of Material: Cementitious
Sample Taken Date: 01/14/2020
Date that the sample was received by the laboratory/organization performing the testing: 01/14/2020
The quantity of what the sample constitutes: 1 Bucket
A brief description of the sample: Type I/II
From where was the sample collected: Source
Laboratory sample identification: CM205004
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: LaFarge

Material Information

Brand: LaFarge
Mill: Richmond
Type of Cementitious Material: Type II Cement

Test Results

Test 1 of 6

DIME Test ID: 2020-01-14-2-2
Test Method: ASTM C109-16a: Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
Verified Date: 01/06/2021
Date Tested: 02/27/2020
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test: 3 day test
Test Result Compliance:
Additional Comments When Verified:
Will control cubes be used per ASTM C311? no
Age of specimen 3 days
The amount of flow no data %
The amount of water used 48.5 %
Compressive strength of 1st specimen 3546 psi
Compressive strength of 2nd specimen 3790 psi
Compressive strength of 3rd specimen 3569 psi
Average Compressive strength (to nearest 10 psi) 3640 psi

Test 2 of 6

DIME Test ID: 2020-01-14-2-3
Test Method: ASTM C109-16a: Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
Verified Date: 01/06/2021
Date Tested: 03/03/2020
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test: 8 day test -- Specimen 3 was eliminated from the average for being outside allowable limits per Section 12 of ASTM C109
Test Result Compliance:
Additional Comments When Verified:
Will control cubes be used per ASTM C311? no
Age of specimen 8 days
The amount of flow no data %
The amount of water used 48.5 %
Compressive strength of 1st specimen 4493 psi
Compressive strength of 2nd specimen 4322 psi
Compressive strength of 3rd specimen 4771 psi
Average Compressive strength (to nearest 10 psi) 4410 psi

Test 3 of 6

DIME Test ID: 2020-01-14-2-4
Test Method: ASTM C109-16a: Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
Verified Date: 01/06/2021
Date Tested: 03/23/2020
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Will control cubes be used per ASTM C311? no
Age of specimen 28 days
The amount of flow no data %
The amount of water used 48.5 %
Compressive strength of 1st specimen 5756 psi
Compressive strength of 2nd specimen 5901 psi
Compressive strength of 3rd specimen 5667 psi
Average Compressive strength (to nearest 10 psi) 5770 psi

Test 4 of 6

DIME Test ID: 2020-01-14-2-5
Test Method: ASTM C185-15a: Standard Test Method for Air Content of Hydraulic Cement Mortar
Verified Date: 01/06/2021
Date Tested: 02/10/2020
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Specific gravity 3.15
Water Content 238
The amount of flow (In percent) 88 %
The amount of water used (In percent) 68.00 %
Net Weight of Sample 843.7 grams
Air Content 7 %

Test 5 of 6

DIME Test ID: 2020-01-14-2-6
Test Method: ASTM C191-13: Standard Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle
Verified Date: 01/06/2021
Date Tested: 02/05/2020
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Type of Water Used Potable
Initial time of setting 120 min
Final time of setting no data

Test 6 of 6

DIME Test ID: 2020-01-14-2-7
Test Method: ASTM C204-11: Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus
Verified Date: 01/06/2021
Date Tested: 01/22/2020
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Method Used Test Method A
Test Time 108 seconds
Fineness 4184 cm^2/g