Testing Report for 2020-01-01-11-4

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 213943 DEA: 051G5704 EFIS: 0515000049 QA Service Level: 1
DIST-CO-RTE-PM: 05-SLO-58-0.7/1.9
Work Description: COLD PLANE AC, PLACE RHMA-G AND RECONSTRUCT CURB RAMPS.
Location Description: SAN LUIS OBISPO COUNTY AT SANTA MARGARITA FROM 0.7 MILE EAST OF ROUTE 101/58 SEPARATION TO J STREET
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Hassan Iman Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-01-01-11
TL Number from the TL Form:
Sample Submitted By Organization: CT D05 - Field Laboratory
Sample Organization Contact: (559) 230-3109
Type of Sample: Quality Control
Type of Material: Hot Mix Asphalt
Sample Taken Date: 01/01/2020
Date that the sample was received by the laboratory/organization performing the testing:
The quantity of what the sample constitutes: 0
A brief description of the sample: RHMA-G
From where was the sample collected: Other
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: CalPortland Paso Robles

Material Information

HMA Type: RHMA-G
HMA Grading: 1/2 inch
Lot number:
Sublot number:

Test Information

DIME Test ID: 2020-01-01-11-1
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Asphalt Binder Content)
Verified Date: 01/17/2020
Date Tested: 01/01/2020
Submitted By Organization: CT D05 - Field Laboratory
Organization Address: 50 Higuera St,
Organization City: San Luis Obispo
Organization State: CA
Organization Zipcode: 93401
Organization Email: doug.lambert@dot.ca.gov
Organization Phone: (559) 230-3109
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified :

Submitted Test Results

Percent Air Voids 4.2 %
Percent Air Voids 2 3.9 %
Percent Air Voids 3 4.2 %
Percent Air Voids Average 4.1 %