Print Report | Back to Sample Detail

Sample Record for 2018-09-11-1

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 211848 DEA: 112T2174 EFIS: 1116000131 QA Service Level: 1
DIST-CO-RTE-PM: 11-SD-5-R37.4 - R46.5
Work Description: (Alternative Delivery) CMGC, San Elijo Highway Bridge Replacement. Replace the San Elijo lagoon highway bridge, construct HOV lanes, construct bike and pedestrian trails and bridge, build multi-use facility at Manchester Ave.
Location Description: IN SAN DIEGO COUNTY IN SOLANA BEACH AND ENCINITAS FROM 0.1 MILE NORTH OF LOMAS SANTA FE DRIVE OVERCROSSING TO 0.2 MILE SOUTH OF BIRMINGHAM DRIVE OVERCROSSING
Contractor Name: Flatiron-Skanska-Stacy and Witbeck, a Joint Venture
Contractor Address: 1770 La Costa Meadows Drive, San Marcos, CA 92078
Resident Engineer: Steve McMillan Structure Rep.: Phong Le

Sample Information

DIME Sample ID: 2018-09-11-1
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - QASI Bay Area Field Office
Sample Organization Contact: (916) 284-6784
Type of Sample: Quality Assurance
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 09/11/2018
Date that the sample was received by the laboratory/organization performing the testing: 09/17/2018
The quantity of what the sample constitutes: 15
A brief description of the sample: Steel-reinforced elastomeric bearing pad
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Scougal Rubber Corp

Material Information

Mfg. Lot Number(s): 16989-1
Material/Compound/Elastomer ID: CP 2527 V
Samples Representing: 796 pads
Description (size): 1.15" x 4" x 6"
Comments:
Description (Number of Shims): 2
Type of Bearing Pad: Steel
Description (Thickness of Shims): 14 gage
Manufacturer(s): Scougal
Batch Number: S288589-V

Test Results

Test 1 of 10

DIME Test ID: 2018-09-11-1-1
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 51
Reading #2 50
Reading #3 50
Reading #4 51
Reading #5 51
Mean 50.6

Test 2 of 10

DIME Test ID: 2018-09-11-1-2
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers-Tension
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 5
Unit of the Ultimate Tensile Values lbf per sqr in
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.073 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 1475.4 lbf/in^2
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.071 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 3033.7 lbf/in^2
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.072 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2888.9 lbf/in^2
Sample 3 Elongation (350% Min) Pass
Sample 4 Median Thickness 0.071 in
Sample 4 Thickness all Within 0.003 inch? Yes
Sample 4 Ultimate Tensile 3033.7 lbf/in^2
Sample 4 Elongation (350% Min) Pass
Sample 5 Median Thickness 0.069 in
Sample 5 Thickness all Within 0.003 inch? Yes
Sample 5 Ultimate Tensile 3063.6 lbf/in^2
Sample 5 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 3033.7 lbf/in^2

Test 3 of 10

DIME Test ID: 2018-09-11-1-3
Test Method: ASTM D624-00-re12: Standard Test Method for Tear Strength of Conventional Vulcanized Rubber and Thermoplastic Elastomers
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 3
UTM no data
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.068 in
Sample 1 Tear Strength 279.4 lbf / in
Sample 2 Median Thickness 0.069 in
Sample 2 Tear Strength 260.9 lbf / in
Sample 3 Median Thickness 0.07 in
Sample 3 Tear Strength 242.9 lbf / in
Median of the Tear Strength Values 260.9 lb/in

Test 4 of 10

DIME Test ID: 2018-09-11-1-4
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers-Tension
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 5
Unit of the Ultimate Tensile Values lbf per sqr in
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.071 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2752.8 lbf/in^2
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.069 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2890.2 lbf/in^2
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.06 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2200 lbf/in^2
Sample 3 Elongation (350% Min) Pass
Sample 4 Median Thickness 0.06 in
Sample 4 Thickness all Within 0.003 inch? Yes
Sample 4 Ultimate Tensile 2666.7 lbf/in^2
Sample 4 Elongation (350% Min) Pass
Sample 5 Median Thickness 0.055 in
Sample 5 Thickness all Within 0.003 inch? Yes
Sample 5 Ultimate Tensile 2753.6 lbf/in^2
Sample 5 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2752.8 lbf/in^2

Test 5 of 10

DIME Test ID: 2018-09-11-1-5
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 50
Reading #2 51
Reading #3 51
Reading #4 50
Reading #5 51
Mean 50.6

Test 6 of 10

DIME Test ID: 2018-09-11-1-6
Test Method: ASTM D624-00-re12: Standard Test Method for Tear Strength of Conventional Vulcanized Rubber and Thermoplastic Elastomers
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 3
UTM no data
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.071 in
Sample 1 Tear Strength 253.5 lbf / in
Sample 2 Median Thickness 0.074 in
Sample 2 Tear Strength 229.7 lbf / in
Sample 3 Median Thickness 0.074 in
Sample 3 Tear Strength 202.7 lbf / in
Median of the Tear Strength Values 229.7 lb/in

Test 7 of 10

DIME Test ID: 2018-09-11-1-7
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 51
Reading #2 51
Reading #3 50
Reading #4 51
Reading #5 50
Mean 50.6

Test 8 of 10

DIME Test ID: 2018-09-11-1-8
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers-Tension
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 3
Unit of the Ultimate Tensile Values lbf per sqr in
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.066 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2484.8 lbf/in^2
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.07 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2800 lbf/in^2
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.07 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2571.4 lbf/in^2
Sample 3 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2571.4 lbf/in^2

Test 9 of 10

DIME Test ID: 2018-09-11-1-9
Test Method: ASTM D624-00-re12: Standard Test Method for Tear Strength of Conventional Vulcanized Rubber and Thermoplastic Elastomers
Verified Date: 10/02/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 3
UTM no data
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.065 in
Sample 1 Tear Strength 230.8 lbf / in
Sample 2 Median Thickness 0.067 in
Sample 2 Tear Strength 209 lbf / in
Sample 3 Median Thickness 0.061 in
Sample 3 Tear Strength 245.9 lbf / in
Median of the Tear Strength Values 230.8 lb/in

Test 10 of 10

DIME Test ID: 2018-09-11-1-10
Test Method: SMTL BILST-06: (Neoprene Verification) Bilstein Test
Verified Date: 10/02/2018
Date Tested: 10/02/2018
Submitted By Organization: CT HQ - Sacramento Chemistry Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: sanchita.dey@dot.ca.gov
Organization Phone: (916) 227-7912
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Result Pass