Testing Report for 2018-04-20-1-2

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: No Project
EFIS:
Project ID: 0
QA Service Level:
DIST-CO-RTE-PM: ---
Work Description: Special project identifier for material not associated with a project
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2018-04-20-1
TL Number from the TL Form:
Sample Submitted By Organization: CT QASI - Bay Area Field Laboratory
Sample Organization Contact: (707) 649-5453
Type of Sample: Stock
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 4/20/2018
Date that the sample was received by the laboratory/organization performing the testing:
The quantity of what the sample constitutes: 1 lot of 30 rolls
A brief description of the sample: .5 bearing pad
From where was the sample collected: Fabricator
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Cal-Neva

Material Information

Mfg. Lot Number(s): 11-27-17
Material/Compound/Elastomer ID: NC 8168
Samples Representing: 30
Description (size): .25" x 8" x 12"
Comments: Contact QAI for tag numbers
Description (Number of Shims): none
Type of Bearing Pad: Plain
Description (Thickness of Shims): NA
Manufacturer(s): Warco Biltrite
Batch Number: 11-27-17

Test Information

DIME Test ID: 2018-04-20-1-2
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension
Date Tested: 4/24/2018
Verified Date: 5/2/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified :

Submitted Test Results

UTM: 11KIP
Humidity: 50 %
Temperature: 72 F
Sample 1 Median Thickness: 0.07 in
Sample 1 Thickness all Within 0.003 inch?: Yes
Sample 1 Ultimate Tensile: 3028.6 lbf/in^2
Sample 1 Elongation (350% Min): Pass
Sample 2 Median Thickness: 0.069 in
Sample 2 Thickness all Within 0.003 inch?: Yes
Sample 2 Ultimate Tensile: 3028.9 lbf/in^2
Sample 2 Elongation (350% Min): Pass
Sample 3 Median Thickness: 0.067 in
Sample 3 Thickness all Within 0.003 inch?: Yes
Sample 3 Ultimate Tensile: 3017.9 lbf/in^2
Sample 3 Elongation (350% Min): Pass
Median of the Ultimate Tensile Values: 3028.6 lbf/in^2