Print Report | Back to Test Summary

Testing Report for 2017-03-07-6-4

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: STOCK
EFIS: STOCK
Project ID: 88888
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2017-03-07-6
TL Number from the TL Form: NA
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM2 - Type B Elastomeric Joint Seal
Sample Taken Date: 3/7/2017
Date that the sample was received by the laboratory/organization performing the testing: 3/15/2017
The quantity of what the sample constitutes: 1
A brief description of the sample: Joint Seal
From where was the sample collected: Manufacturer
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: DS Brown

Material Information

Mfg. Lot Number(s): 0117103
Manufacturer(s): DS Brown
Temperature: 72
Humidity: 45
Comments: Unknown
Joint Seal Size: 5

Test Information

DIME Test ID: 2017-03-07-6-4
Test Method: ASTM D2628-91-re11-low: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (Low Temp Recovery)
Date Tested: 3/24/2017
Verified Date: 4/3/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified :

Submitted Test Results

Temperature: 72 f
Humidity: 50 %
Low Temp Recovery (22 hrs at -20F) Size Before (Height of Contact Face ): 5 in
Low Temp Recovery (22 hrs at -20F) Size After (Recovered Contact Face ): 4.672 in
Percent Recovery (Low Temp): 93 %