Print Report | Back to Test Summary

Testing Report for 2016-12-02-2-5

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 59912684
EFIS:
Project ID: 8196
QA Service Level: 1
DIST-CO-RTE-PM: 59---
Work Description:
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2016-12-02-2
TL Number from the TL Form: NA
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM2 - Type B Elastomeric Joint Seal
Sample Taken Date: 12/2/2016
Date that the sample was received by the laboratory/organization performing the testing: 12/5/2016
The quantity of what the sample constitutes: 550ft
A brief description of the sample: Joint Seal
From where was the sample collected: Manufacturer
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Watson Bowman

Material Information

Mfg. Lot Number(s): 1416426
Manufacturer(s): Watson Bowman
Temperature: 72
Humidity: 50
Comments: Unknown
Joint Seal Size: 3.75

Test Information

DIME Test ID: 2016-12-02-2-5
Test Method: ASTM D2628-91-re11-high: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (High Temp Recovery)
Date Tested: 12/12/2016
Verified Date: 12/21/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Temperature: 72 f
Humidity: 50 %
High Temp Recovery (70 hrs at 212F) Size Before (Height of Contact Face ): 3.75 in
High Temp Recovery (70 hrs at 212F) Size After (Expanded Contact Face ): 3.611 in
Percent Recovery (High Temp): 96 %