Print Report | Back to Test Summary

Testing Report for 2016-02-23-4-4

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: STOCK
EFIS: STOCK
Project ID: 88888
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2016-02-23-4
TL Number from the TL Form: Unknown
Sample Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Sample Organization Contact: (916) 227-7071
Type of Sample: Annual Source Testing
Type of Material: Cementitious
Sample Taken Date: 2/23/2016
Date that the sample was received by the laboratory/organization performing the testing: 9/6/2016
The quantity of what the sample constitutes: 1 Bucket
A brief description of the sample: Type II Cement
From where was the sample collected: Source
Laboratory sample identification: CM165656
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Lehigh Yadong China

Material Information

Brand: Lehigh Yadong Chna
Mill: Yadong China
Type of Cementitious Material: Type II Cement

Test Information

DIME Test ID: 2016-02-23-4-4
Test Method: ASTM C191-13: Standard Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle
Date Tested: 9/14/2016
Verified Date: 3/20/2019
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test: CM165656
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Type of Water Used: Type III grade reagent water
Time in minutes of last penetration greater than 25mm (E): 175 min
Time in minutes of first penetration less than 25mm (H): 180 min
Penetration reading at time E : 27 mm
Penetration reading at time H: 22 mm
Initial time of setting: 177 min
Final time of setting: no data
Method Used: Test Method A